Article
Wear rate of epoxy resin reinforced with multi walls carbon nanotubes
معدل البلى لراتنج الايبوكسي المدعم بأنابيب الكربون النانوية متعددة الجدران

Authors: Ayad Qabash Hameed اياد قباش حميد --- Faik Hammad Anter فائق حماد عنتر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2019 Volume: 17 Issue: 40 Pages: 1-9
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study, nanocomposites have been prepared by adding multiwall carbon nanotubes (MWCNTs) with weight ratios (0, 2, 3, 4, 5) wt% to epoxy resin. The samples were prepared by hand lay-up method. Influence of an applied load before and after immersion in sodium hydroxide (NaOH) of normality (0.3N) for (15 days) at laboratory temperature on wear rate of Ep/MWCNTs nanocomposites was studied. The results showed that wear rate increases with increasing the applied load for the as prepared and immersed samples and after immersion. It was also found that epoxy resin reinforced with MWCNTs has wear rate less than neat epoxy. The sample (Ep + 5wt% of MWCNTs) has lower wear rate. The immersion effect in base solution led to increase in wear rate values for all samples compared to natural condition.

تم في هذا البحث تحضير عينات المتراكبات النانوية باستخدام تقنية القولبة اليدوية بإضافة نسب وزنية %(0، 2، 3، 4، 5) من أنابيب الكربون النانوية متعددة الجدران الى راتنج الإيبوكسي. حيث تمت دراسة تأثير الحمل المسلط قبل وبعد الغمر بمحلول هيدروكسيد الصوديوم ذو عيارية (0.3N) ولمدة (15) يوم على معدل البلى للمواد المتراكبة النانوية ومقارنتها بالحالة الطبيعية (قبل الغمر). بينت نتائج الدراسة ان معدل البلى يزداد مع زيادة الحمل العمودي المسلط ولجميع العينات. كما وُجد ان عينات الإيبوكسي المدعمة بأنابيب الكربون النانوية تمتلك معدل بلى اقل مقارنة بالإيبوكسي النقي. اقل قيمة لمعدل البلى سُجلت بالنسبة ل( Ep + 5wt% من MWCNTs). أدى تأثير الغمر بالمحلول القاعدي الى زيادة معدل البلى بالنسبة لجميع العينات مقارنة بالحالة الطبيعة.


Article
Effect of tempering on thermal analysis of Al-Ti-Si alloy and its composites
تأثير المراجعة على التحلل الحراري لسبيكة المنيوم – تيتانيوم – سليكون والمواد المتراكبة العائدة لها

Authors: Rana Afif Anaee رنــا عفيف مجيد --- Wafaa Mahdi Salih وفــاء مهدي صالح --- Ban Farhan Dawood بان فرحان داود
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2016 Volume: 14 Issue: 31 Pages: 89-98
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The investigation of the effect of tempering on thermal analysis of Al-Ti-Si alloy and its composites with MgO and SiC particles was performed. Thermal analysis was performed before and after tempering by DSC scan. Optical microscopy was used to identify the phases and precipitations that may be formed in base alloy and composites. X-ray diffraction test indicated that the Al3Ti is the main phase in Al-Ti-Si alloy in addition to form Al5Ti7Si12 phase. Some chemical reactions can be occurred between reinforcements and matrix such as MgO.Al2O3 in Al-Ti/MgO, and Al4C3 and Al(OH)3 in Al-Ti/SiC composite. X-ray florescence technique is used to investigate the chemical composition of the fabricated specimens. Heat treatment (Tempering) changes the microstructure of base alloy and its composites which was assessed by DSC scan. Generally, three main peaks appeared in DSC represented by GP zone, S phase (precipitations) and dissolution of phases or precipitations. After tempering, composite with SiC particles showed better results than base alloy and composite with MgO. Since the optical microscopy revealed reforming the stable phase Al3Ti with evaporation some gases from composite. DSC analysis showed the stability ofcomposite with SiCwas up to 270oC.DSC, Al-Ti-Si alloy, Composite, SiC, MgO, Al3Ti phase, Al5Ti7Si12.

لقد تم الكشف عن تأثير المراجعة على التحليل الحراري لسبيكة المنيوم – تيتانيوم – سليكون مع مواده المتراكبة المدعمة باوكسيد المغنيسيوم وكاربيد السليكون بنسبة وزنية 1% من خلال فحص المسعر التفاضلي الحراري. اجري فحص البنية بالمجهر البصري لتشخيص الاطوار المتكونة في السبيكة الاساس والمواد المتراكبة المدعمة وقد اثبت فحص الحيود بالاشعة السينية تكون الطور الرئيسي Al3Ti بالاضافة الى تكوين الطور Al5Ti7Si12 بالاضافة الى اطور اخرى تتكون ضمن المواد المتراكبة مثل MgO.Al2O3و Al4C3 و Al(OH)3واطوار اخرى. ان المعاملة الحرارية تغير من تفاعلات التبلور والانصهار الظاهرة في فحص التحلل الحراري باستخدام المسعر الماسح التفاضلي. ان قمم التبلور الرئيسية الظاهرة في فحص التحلل الحراري هي ظهور طبقة GP وقمة الطور البيني S وقمة الاطوار غير المتماسكة. ان المادة المتراكبة المدعمة بدقائق كاربيد السليكون تظهر من خلال الفحص بالمسعر الماسح التفاضلي استقراراً حرارياً واظحاً الى حد 270 درجة مئوية.