Structural and Optical Properties of ZnS Thin Films Prepared by SprayPyrolysis Technique

Author: Nada M. Saeed
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2011 Volume: 14 Issue: 2 Pages: 86-92
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Zinc Sulfide (ZnS) is important II-VI semiconductors material for the development of various
modern technologies and photovoltaic applications. ZnS thin film was prepared by using chemical
spray pyrolysis technique. The spray solutions contains ZnCl2 and SC(NH2)2 with molar
concentration 0.1M/L. ZnS thin films was growth onto hot glass substrates at substrates temperature
400оC.
The Structure of the prepared film was studied from X-ray diffraction pattern, the results shows
that the film was polycrystalline with hexagonal structure, the grain size of ZnS film was calculated,
it was 139 Å at the high peak.
The optical properties of the film were studied using measurement from UV–VIS
spectrophotometer; the results appear that a good optical transparency of about 65 % was observed
in the visible region. The optical constants were studied as a function of the photon energy within
the wavelength in the range (300-900) nm. The refractive index was calculated in the visible region,
it was 2.45 at 500 nm. The optical band gaps for the direct and indirect transition were estimate too
and it was 3.2 – 3.1 eV respectively.

الخلاصةيعتبر كبريتيد الزنك من أشباه الموصلات المهمة نوع II-VI وذلك لدخوله في العديد من التقنيات الحديثة وكذلك في تطبيقات الخلايا الفوتوفولتائية. تم تحضير مجموعة من الأغشية الرقيقة لمركب كبريتيد الزنك باستخدام تقنية الرش الكيميائي الحراري، تم تحضير محلول الرش المتكون من خلط نسب معينة من كلوريد الخارصين والثايوريا بمولارية مقدارها 0.1 M/L وقد تكونت أغشية كبريتيد الخارصين الرقيقة على شرائح زجاجية ساخنة بدرجة حرارة أساس400OC .درست الخواص التركيبية للغشاء المحضر من خلال الفحص بواسطة حيود الأشعة السينية، وقد أظهرت النتائج أن الغشاء المحضر نوع متعددة التبلور (Polycrystalline). تم حساب الحجم الحبيبي وكانت قيمته 139 Å عند أعلى قمة.تم دراسة الخواص البصرية لغشاء ZnS باستعمال مطياف يعمل ضمن الأطوال الموحية المرئية وفوق البنفسجية .VIS-UV أظهرت الدراسة البصرية بان معدل النفاذية تقترب من 65% عند المدى المرئي. تم حساب الثوابت البصرية كدالة لطاقة الفوتون لمدى الاطوال الموجية nm 300-900. وكانت قيمة معامل الأنكسار ضمن المدى المرئي2.45 عند 500 nm. اما قيم فجوة الطاقة للانتقالات الالكترونية المباشرة والغير مباشرة فكانت 3.2 eV و 3.1 eVعلى التوالي.


Article
ENHANCEMENT THE OPTICAL PROPERTIES OF ZINC SULFIDE THIN FILMS FOR SOLAR CELL APPLICATIONS
تحسين الخواص البصرية لأغشية كبريتيد الزنك الرقيقة لتطبيقات الخلايا الشمسية

Authors: A. M. Suhail عبد الله محسن سهيل --- Nada M. Saeed ندى محمد سعيد
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2012 Volume: 53 Issue: 1 Pages: 88-95
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this work, semi-conducting ZnS compound was prepared as thin films onto glass substrates at two different substrates temperature (673, 723) K using chemical spray pyrolysis technique. X-ray diffraction was studied for the prepared films, the results shows that the films was polycrystalline with a wurtzite (hexagonal) structure. The optical properties of the films were studied by using VIS-UV spectrophotometer, the absorbance and transmittance spectrum have been recorded at wavelength within the range (300-900) nm. The optical characteristics were studied as a function of the photon energy at the mentioned wavelength. The results appear that the transparency of the films at visible region is rise from 70% to 90% at high substrates temperature. The refractive index was estimated within the visible wavelength at 500 nm, it was 2.45 at substrate temperature 673 K and its value will decrease at the highest substrate temperature. The direct optical band gap of the allow transitions for the deposits films prepared at both substrate temperatures (673, 723) K were varied from 3.2-3.4 eV respectively.

في هذا البحث, تم تحضير مجموعة من الأغشية الرقيقة لمركب كبريتيد الزنك باستخدام تقنية الرش الكيميائي الحراري على شرائح زجاجية بدرجتي حرارة أساس مختلفة (673-723)K. تم فحص الأغشية المحضرة بواسطة حيود الأشعة السينية, ومن دراسة النتائج تبين أن جميع الأغشية المحضرة هي نوع متعددة التبلور (Polycrystalline).تم دراسة الخواص البصرية لأغشيةZnS باستعمال مطياف يعمل ضمن الأطوال الموجية المرئية وفوق البنفسجية .VIS-UV اشتملت دراسة الخواص البصرية على تسجيل طيفي الامتصاصية والنفاذية للأغشية المحضرة لمدى الأطوال الموجية nm 300-900, تم دراسة الخواص البصرية كدالة لطاقة الفوتون عند مدى الأطوال الموجية المذكورة أظهرت النتائج بان معدل النفاذية يرتفع من 70% الى 90% في المدى المرئي عند ارتفاع درجة حرارة الأساس. تم حساب معامل الانكسار ضمن المدى 500 nm من الطول ألموجي وكانت قيمته 2.45.عند درجة 673 K وتكون قيمته أقل عند زيادة درجة حرارة الأساس. هذا وتتغير قيم فجوة الطاقة للانتقالات الالكترونية المباشرة عند درجتي حرارة القاعدة الزجاجية 673) K و ( 723من 3.2 eV إلى 3.4 eV على التوالي.

Listing 1 - 2 of 2
Sort by
Narrow your search

Resource type

article (2)


Language

Arabic and English (1)

English (1)


Year
From To Submit

2012 (1)

2011 (1)