Article
Mechanical Properties of Unsaturated Polyester Filled With Silica Fume, Glass Powder and Carbon Black

Authors: A.H. Majeed --- S.Q. Ibrahim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 6 Part (A) Engineering Pages: 640-647
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this study a polymer matrix composites (PMCs) have been prepared with the aid of ultrasonic wave dispersion method for mixing , using of unsaturated polyester resin with Silica Fume(SF), Glass Powder (GP)and Carbon Black (CB). Moulds were prepared by hand-made from silicon rubber according to the ASTM standard table (4). The fillers added separately with different ratios as (0%,0.5%, 1%, 1.5 %, 2%,2.5% and 3%).The results show increase the hardness and impact strength when added GP, SF, and CB to polymer matrix. Flexural strength and maximum shear stress decrease when added silica fume , but when added glass powder and carbon black led to increase flexural strength and maximum shear stress to certain percent at ( 2%, 1.5% for GP and CB respectively) then dropped when increase weight fraction of GP, CB . Compressive strength decrease when added glass powder and carbon black, while it is increase when added silica fume to polymer matrix. Wear rate decrease when increase weight fraction of carbon black but it increases when added GP and SF.


Article
Preparation of unsaturated polyester/nano ceramic composite and study electric, thermal and mechanical properties
تصنيع متراكبات بولي استر الغير المشبع /نانو سيراميك ودراسة الخواص الكهربائية و الحرارية و الميكانيكة

Authors: Shatha H. Mahdie شذى هاشم مهدي --- Qasem Abd Saloom قاسم عبد سلوم --- Duna Sami Abd Alaziz دنى سامي عبد العزيز
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2017 Volume: 15 Issue: 35 Pages: 188-201
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The composites were manufactured and study the effect of addition of filler (nanoparticles SiO2 treated with silane) at different weight ratios (1, 2, 3, 4 and 5) %, on electrical, mechanical and thermal properties. Materials were mixed with each other using an ultrasound, and then pour the mixture into the molds to suit all measurements. The electrical characteristics were studied within a range of frequencies (50-1M) Hz at room temperature, where the best results were shown at the fill ratio (1%), and thermal properties at (X=3 %), the mechanical properties at the filler ratio (2%).

تم تصنيع المركبات ودراسة تأثير إضافة الحشو (الجسيمات النانوية SiO2 المعالجة سطحيا) بنسب وزنية مختلفة 5)و (1, 2, 3, 4 %، على الخصائص الكهربائية والميكانيكية والحرارية. خلطت المواد مع بعضها البعض باستخدام جهاز الموجات فوق الصوتية، ثم صب الخليط في قوالب لتناسب جميع القياسات. درست الخصائص الكهربائية ضمن مجموعة من الترددات (50-1M) Hzفي درجة حرارة الغرفة، حيث أظهرت أفضل النتائج عند نسبة التعبئة (1%) والحرارية عند ( X=3%)، الخواص الميكانيكية عند نسبة حشو (2%).


Article
Effect of Reinforced by Zinc Oxide Powder on the Mechanical Properties forUn-saturated Polyester Matrix Composite Material
تأثير التقوية بمسحوق أوكسيد الزنك على الخواص الميكانيكية لمادة متراكبة ذات أساس من البولي أستر غير المشبع

Author: هناء عرير سميج
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 10 Pages: 474-484
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research is devoted to the preparation of polymer matrix composite materials by (Hand Lay-Up ) method, where the composite material was prepared from the unsaturated polyester resin (UP) as a matrix reinforced by Zinc Oxide with volume fractions (0% , 1% , 2% , 3% ,4% ) .several of mechanical tests were done and these includes Impact, Bending, Flexural Strength, Shear Stress and Hardness, Result of thetests shows that the values of (Bending elastic modulus, Flexural Strength , Fracture Toughness, Hardness and Shear Stress) increase with the increase of Zinc Oxide particle volume fraction, but the values of Impact Strength decreased with the increases of volume fraction of Zinc Oxide particles.


Article
Improving the thermal insulation property of polyester resin
تحسين العزل الحراري للبولي استر بإضافة الألياف الزجاجية

Author: Safaa A. S. Almtori , Abdul khaliq A. Hasan and Maitham Y. Atshan
Journal: Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) ISSN: 18172695 Year: 2010 Volume: 36 Issue: 2A Pages: 10-15
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

The aim of this research is to study the effect of fiber glass on the thermal insulation property of polyester resin . Different amounts of fiber glass were added to the polyester resin with hardener then cast as sheet of composite material of dimension (20*20*0.3) cm3 with different fiber glass weight percentage : ( 0% , 4 % , 8 % , 12 % , 16 % , 20 % ) of the total weight. The thermal conductivity was calculated by using Lee’s Disk method . The mean value of five measurements of thermal conductivity ( k ) for each specimen was measured , also the hardness of the specimens was measured by using shore method type D and then sketch the relation between thermal conductivity and hardness with the percentage of fiber glass. The results showed that the thermal conductivity (k) of polyester decreased (which mean thermal insulation increased ) with an increase of fiber glass percentage , and the hardness increased with the increase of fiber glass percentage due to the restricted movement of the chain end of polymer .

يهدف هذا البحث إلى دراسة تأثير إضافة الألياف الزجاجية إلى البولي استر على خاصية العزل الحراري ، وكذلك على الصلادة .حيث تم إضافة كميات مختلفة من الألياف الزجاجية مع البولي استر المخلوط بمادة مصلبة لتكوين شرائح من المادة المركبة ذات أبعاد ( 20 * 20 * 0.3 ) سم3 . تم تحضير ست عينات يختلف فيها نسبة وزن الألياف الزجاجية المضافة وهي ( 0 % ، 4 % ، 8 % ، 12 % ، 16 % ، 20 % ) على التوالي من الوزن الكلي لكل عينة مستخدمة. تم حساب التوصيل الحراري باستخدام طريقة Lee’s Disk ، وذلك باستخدام قيم مختلفة للتيار الكهربائي وحساب معدل التوصيل الحراري ( k ) لكل عينة . كذلك تم قياس صلادة العينات باستخدام طريقة شور للصلادة نوع D . من رسم العلاقة بين كل من التوصيل الحراري ( k ) والصلادة مع النسب المئوية المختلفة لمادة الألياف الزجاجية المستخدمة لوحظ الآتي : انخفاض مقدار التوصيل الحراري k ( أي زيادة العزل الحراري ) وزيادة الصلادة ، كلما زادت نسبة الألياف الزجاجية المستخدمة .


Article
Study the Synergetic Activity of Aluminium Tri Hydroxide with Zinc Oxide as Flame Retardants for Unsaturated Polyester Resin
دراسة الفعل التازري لهيدروكسيد الالمنيوم مع اوكسيد الخارصين كمثبطات للهوبية البولي استر غير المشبع

Authors: Jalil R. Ugal --- Rawnaq B. Jimaa
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 1 Issue: المؤتمر العلمي الاول للتربية للعلوم الصرفة Pages: 43-50
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this work, aluminum tri hydroxide (I), zinc oxide (II) and their mixture (1:1) (III) were used as flame retardants for unsaturated polyester resin in the weight ratios of (0, 2, 4, 7, 10, and 12) %, by preparing films of (130*130*3) mm in dimensions.Three standard test methods used to measure the flame retardation which are: ASTM: D-2863 to measure the limiting oxygen index (LOI), ASTM: D-635 to measure the rate of burning (R.B) & ASTM: D-3014 to measure the maximum height of flame (H). Results obtained from these tests indicated that; ATH, ZnO and their mixture have a good effect as flame retardants for unaturated polyester resin. The synergetic effect was the best.

في هذا البحث تم استخدام هيدروكسيد الالمنيوم (مضاف I), اوكسيد الخارصين(مضاف II) ومزيجهما بنسبة (1:1) مضاف (III) كمثبطات للهوبية البولي استر غير المشبع. بنسب مئوية وزنية (10, 7, 4, 2, 0و 12) % بواسطة تحضير شرائح بابعاد (130*130*3) ملم.استخدمت ثلاث طرق قياسية لاختبار تثبيط اللهوبية وهي: الطريقة القياسية (( LOI ASTM: D-2863 لقياس معامل الاوكسجين المحدد, الطريقة القياسية ASTM: D-635 لقياس سرعة الاحتراقوالطريقة القياسية ASTM: D-3014 لقياس اقصى ارتفاع يصل اليه اللهب(H) اظهرت النتائج المستحصل عليها ان المضافات المستعملة في هذه الدراسة تمتلك تاثير جيدا كمثبطات لهب للبولي استر غير المشبع. وان افضلها كانت عندما كان التاثيرتازريا


Article
Effect Of Reinforced by Coconut Fiber Core on The Mechanical Properties for Un-Saturated Polyester Matrix Composite Material
تاثیر التدعیم بالیاف ثمرة جوز الھند على الخواص المیكانیكیة لمادة متراكبة ذات اساس من البولي استر غیر مشبع

Author: Hind Basil Ali ھند باسل علي
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 17 Part (A) Engineering Pages: 296-308
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This work involves study tensile strength; hardness and thermal conductivity ofcomposite material consist of coconut fibers mixed with polyester resin. Thiscomposite material was prepared by adding three percentage of coconut shells (1,2 and3) wt% . addition of coconut shells improved mechanical properties for compositematerial with three percentages , while led to decrease thermal conductivity because itis behave as insulated material.


Article
Study the Effect of Different Percentages of Natural (Orange Peels and Date Seeds) and Industrial Materials (Carbon and Silica) on the Mechanical and Thermal Properties of Polymeric Reinforced Composites
دراسة تاثير اضافة المواد الطبيعية (نوى التمر وقشور البرتقال) والصناعية (الكاربون والسليكا) على الخواص الميكانيكية والحرارية للمواد المركبة البولمرية

Authors: Haydar Abed Dahad حيدر عبد ضهد --- Sameh Fareed Hasan سامح فريد حسن --- Ali Hussein Alwan علي حسين علوان
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2018 Volume: 14 Issue: 4 Pages: 16-23
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Mechanical and thermal properties of composites, consisted of unsaturated polyester resin, reinforced by different kinds of natural materials (Orange peels and Date seeds) and industrial materials (carbon and silica) with particle size 98 µm were studied. Various weight ratios, 5, 10, and 15 wt. % of natural and industrial materials have been infused into polyester. Tensile, three-point bending and thermal conductivity tests were conducted for the unfilled polyester, natural and industrial composite to identify the weight ratio effect on the properties of materials. The results indicated that when the weight ratio for polyester with date seeds increased from 10% to 15%, the maximum Young’s modulus decreased by 54%. When the weight ratio was 5%, the maximum Young’s modulus, yield stress and ultimate tensile stress occurred in the polyester with date seeds. The results of tensile and flexural tests showed that the natural composite material has a higher strength than the industrial material. While the results of flexural tests manifested that the maximum improvement in the flexural strength is obtained for orange peels at 5 wt. %, where the maximum increasing percentage is 153.4% than pure polyester. The thermal conductivity of orange peels decreased to the half value when the weight ratio increased from 10% to 15%. The thermal conductivity for polyester with orange peels was greater than the thermal conductivity of polyester with date seeds with maximum percentage occurred at weight ratio 10% is 14.4%, but the thermal conductivity of the industrial composite material was higher than the natural composite material. Finally, the date seeds composite was a good insulator and it had a reduced heat transfer rate in comparison to the rest of the samples, also the maximum variation of temperature with time occurred in date seeds composite.

تم دراسة الخصائص الميكانيكية والحرارية للمواد المركبة التي تتكون من بولي استر غير مشبع المقواة بأنواع مختلفة من المواد الطبيعية (قشر البرتقال ونوى التمر) والمواد الصناعية (الكربون والسيليكا) مع حجم حبيبي 98 ميكرون. تم اخذ قيم متلفة من النسب الوزنية، %5و %10و 15%. وقد تم اضافة مواد صناعية ومواد طبيعية الى البولي استر. وقد تم أجراء اختبارات الشد و الانحناء والتوصيل الحراري للبولي استر والمواد المركبة الطبيعية والصناعية لتحديد تأثير النسبة الوزنية على خصائص المواد. وأظهرت النتائج أنه عندما زادت نسبة الوزن للبوليستر مع نوى التمر من 10٪ إلى 15٪، انخفض معامل المرونة بنسبة 54٪. عندما تكون النسبة الوزنية لنوى التمر5٪ الحد الأقصى لمعامل المرونة والإجهاد الخضوع والإجهاد الكسر. وأظهرت نتائج اختبارات الشد واالانحناء أن المواد المركبة الطبيعية لها قوة أعلى من المادة الصناعية. في حين أظهرت نتائج اختبارات الانحناء أن الحد الأقصى من التحسن في قوة الانحناء يتم الحصول عليه لقشور البرتقال بنسبة 5٪ ، حيث الحد الأقصى لزيادة هي 153.4٪ بالمقارنة مع البوليستر النقي. وانخفضت الموصلية الحرارية من قشور البرتقال إلى قيمة النصف عندما زادت النسبة الوزنية من 10٪ إلى 15٪. الموصلية الحرارية للبوليستر مع قشور البرتقال أكبر من الموصلية الحرارية من البوليستر مع نوى التمر. وكانت النسبة المئوية القصوى عند النسبة الوزنية 10٪ هي 14.4٪ ولكن التوصيل الحراري للمواد المركبة الصناعية اعلى من المواد المركبة الطبيعية. وأخيرا، فإن المركب نوى التمر هو عازل جيد وله معدل نقل حراري منخفض بالمقارنة مع بقية العينات، وكذلك الاختلاف الأقصى لدرجات الحرارة مع مرور الوقت في مركب نوى التمر.


Article
Preparation and Study Hardness and Thermal Conductivity (Tc) to Polyester Resin Composite with (Titanium Dioxide, Zinc Oxide, Acrylonitril, Wood Flour Coconut
تحضير ودراسة الصلادة والتوصيلية الحرارية لمتراكبات راتنج البولي استر مع (ثاني اوكسيد التيتانيوم، اوكسيد الزنك، قلفة ثمرة جوز الهند)

Authors: Asmiet R. Al-Hadithy عصمت رمزي الحديثي --- Khalil Th. Hassan خليل ثابت حسان --- Tariek A. Al- Anie طارق عبد الجليل العاني
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2010 Volume: 7 Issue: 4 Pages: 1400-1409
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study is attempt to improve thermal isolation through measuring thermal conductivity composite of on polyester resin with fillers of (TiO2, ZnO, Acrylonitril, wood flour Coconut (Wf). The grain size of the fillers is 200 µm. The number of samples is (16) in addition to the virgin sample; these samples are prepared by cast molding method for polyester with filler volume fractions (5%, 10%, 15% and 20%). Shore hardness tests were used to measure the hardness and Lee disk method for thermal conductivity. The experimental results showed that the (20% ZnO) sample has the maximum value of thermal conductivity where (20% w.f) has minimum thermal conductivity .on the other hand (15% ZnO) sample give the maximum value of hardness where (20% w.f) sample gave the minimum value of hardness. From this study there is an important factor that should be observed that is the relationship between hardness and thermal conductivity. The study prove that the experimental results satisfy the theoretical assumptions in that the additive material (fillers) of metals base increase thermal conductivity where the material of cellulose base decrease the thermal conductivity and give good thermal isolation but with low hardness and all the result above the refry sample .

تمت في هذه الدراسة محاولة تحسين العزل الحراري من خلال قياس التوصيل الحراري لمتراكبات رانتج البول استر (Matrix) مع حشوة (Filler) هي (TiO2,ZnO،الاكريلونايترايل،ومسحوق قلفة ثمرة جوز الهند W.F والحجم الحبيبي لهذه المواد هو (200µm) اذ تم تحضير(16) ست عشرة عينة بطريقة القولبة بالصب اليدوي (Hand molding casting ) وكانت نسبة الراتنج للبولي استر المضاف اليه الحشوات بتراكيز (20%,15%,10%,5%) واجريت فحوصات الصلادة بطريقة شور(Shore) والتوصيل الحراري باستخدام قرص لي (Lee Disk) وأظهرت النتائج ان اقل توصيل حراري هو الانموذج ذو النسبة (20% W.F coconut) وان أعلى توصيل حراري هو الانموذج ذو النسبة(20% ZnO) وان اوطا قيمة للصلادة هي للانموذج (20% W.F) وأعلى قيمة صلادة هي للانموذج (15% ZnO) وتبين لنا من خلال هذه الدراسة إن هناك عامل مهم يجب ملاحظته هو وجود علاقة بين الصلادة والتوصيل الحراري وأثبتت الدراسة إن المعطيات العملية التجريبية تماشت مع الافتراضات النظرية في ان المواد المضافة ذات الأساس الفلزي تزيد التوصيل الحراري وعلى العكس فان المواد ذات الأصل السللوزي تقلل من التوصيل الحراري وتعطي عزلا جيدا على حساب الصلادة وكانت القيم في جميع الفحوصات أفضل من المرجع للصلادة والتوصيل الحراري.


Article
Effect of carbon nanotube and Zn particles addition on the some mechanical properties and thermal conductivity of unsaturated polyester resin
تأثير انابيب الكاربون النانوية وجسيمات الخارصين المضافة على بعض الخواص الميكانيكية و معامل التوصيل الحراري لراتنج البولي استر غير المشبع

Authors: N.A.Ali نادية عباس علي --- S.I.Husaen سيناء ابراهيم حسين --- H.I.Jaffer حارث ابراهيم جعفر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2012 Volume: 10 Issue: 18 Pages: 98-104
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research work a composite material was prepared contains a matrix which is unsaturated polyester resin (UPE) reinforced with carbon nanotube the percentage weight (0.1, 0.2, 0.4.0.5) %, and Zn particle the percentage weight (0.1, 0.2,0.4,0.5)%.All sample were prepared by hand lay-up, process the mechanical tests contains hardness test, wear rate test, and the coefficient of thermal conductivity. The results showed a significant improvement in the properties of overlapping, Article containing carbon nano-tubes and maicroparticles of zinc because of its articles of this characteristics of high quality properties led to an, an increase in the coefficient of the rmalconductivity, and increase the hardness values with increased percentage weight when the wear rate increase with increased the applied load and percentage weight.

تم في هذا البحث تحضيرمادة متراكبة من راتنج البولي استرغير المشبع مقواة بانابيب الكاربون النانوية وجسيمات الخارصين وبنسب وزنية 0.2)و0.4و0.8و(1%واستخدمت طريقة القولبة اليدوية في تحضير العينات واجريت اختبارات ميكانيكية تضمنت فحص الصلادة وفحص معدل البلى وقياس معامل التوصيل الحراري.اظهرت النتائج تحسنا كبيرا في خواص المادة المتراكبة الحاوية على انابيب الكاربون النانوية وجسيمات الخارصين لما تتمتع به هذه المواد من خصائص عالية الجودة ادت الى زيادة في معامل التوصيل الحراري وزيادة قيم الصلادة بزيادة النسب الوزنية ومعدل البلى كان يزداد بزيادة الحمل المسلط وزيادة النسب الوزنية .


Article
The Diffusion Coefficients of Different Types of Liquid Environments Into Binary Polymer Blend

Authors: Awham M. Hameed --- Raghad H. Helal
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2013 Volume: 16 Issue: 3 Pages: 148-158
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this study, unsaturated polyester resin (UPE) and Natural rubber (NR) were used to prepared binary polymer blend (UPE/ NR) with weight ratio (95/5) %. The present paper investigates the diffusion behavior of three environmental groups , the first group is different types of water included (distilled water, tap water, rain water), the second is diluted solutions with same concentration (HCl , H2SO4, NaCl) and the third is solvents (ethanol, kerosene, benzene) and study their effects through (UPE/NR) polymer blend. Consequently, a set of specimens were immersed in various types of water, solutions and solvents for different periods of time. The diffusion coefficients (Dx) of these liquids were calculated based on Fick's law. The results of a series of experimental investigations showed that the values of (Dx) of all liquids are in the range (3.95- 9.1 *10-12 m2/s) except benzene which behaves another behavior called (non- Fickian diffusion) through the same time of immersion.

في هذا البحث، أستخدم راتنج البولي استر غير المشبع (UPE) والمطاط الطبيعي (NR) لتحضير خليط بوليمري ثنائي (UPE/ NR) وبنسبة وزنية (95/5) %.الدراسة الحالية تبحث السلوك الانتشاري لثلاثة مجاميع بيئية , المجموعة الاولى هي انواع مختلفة من المياه شملت (الماء المقطر, ماء الحنفية, ماء المطر) والثانية هي محاليل مخففة وبنفس التركيز (HCl , H2SO4, NaCl) والثالثة هي مذيبات (الايثانول، النفط، البنزين) ودراسة تاثيراتها خلال الخليط البوليمري (UPE/NR). ولذلك غمرت مجموعة من النماذج في الانواع المختلفة من المياه والمحاليل والمذيبات لفترات زمنية مختلفة. معاملات الانتشار (Dx) لتلك السوائل تم حسابها على اساس قانون فك. اظهرت النتائج لسلسلة من البحوث التجريبية بأن قيم معاملات الانتشار ((Dx لجميع السوائل في المدى 3.95-9.1*10-12)m2/s.) ماعدا البنزين الذي يسلك سلوكا مغايرا حيث لايتبع سلوك فك في الانتشار خلال نفس الفترة من الغمر ويصطلح عليه (non- Fickian diffusion).

Listing 1 - 10 of 36 << page
of 4
>>
Sort by
Narrow your search

Resource type

article (36)


Language

English (20)

Arabic (12)

Arabic and English (4)


Year
From To Submit

2019 (1)

2018 (1)

2017 (4)

2016 (6)

2015 (3)

More...