Behavior of Short Reinforced Porcelinite Concrete Columns Under Concentric Loads
تصرف الأعمدة الخرسانیة المسلحة القصیرة المصنوعة من ركام البورسلینایت تحت الاحمال المركزية

Authors: Kaiss F. Sarsam --- Ihsan A. S. Al-Shaarbaf --- Mustafa S. Shuber
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 6 Pages: 1219-1233
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This study presents on experimental method to investigate the behavior ofreinforced porcelinite concrete columns subjected to concentric load. The experimentalwork includes investigation of ten lightweight concrete columns with square crosssection 190×190mm and 1000mm in length subjected to concentric load to assess theeffect of the amount of longitudinal steel reinforcement, lateral tie reinforcement andgrade of concrete. From the experimental observation it was found that the porceliniteaggregate is a good structural material to produce lightweight concrete columns. It isnoted from tested columns that keeping the amount of the longitudinal steel ratioconstant, the increase in the amount of transverse steel to about four times (bydecreasing the spacing to about a quarter according to the ACI-Code (318M-05)) gave asignificant influence on column post-cracking behavior. The improvements in thecolumn due to higher value of confinement include: (i) less brittle behavior; (ii)significantly less damage to the concrete core; (iii) 12% increase in column loadcarrying capacity. Also, A modified formula for column capacity is proposed to takeinto account the influence of spacing of ties (effect of confinement).

تقدم هذه الدراسة بحثا عمليا لدراسة سلوك الاعمدة الخرسانية خفيفة الوزن التي تحوي علىركام البورسلنايت تحت تاثير الاحمال المحورية . يتضمن الجزء المختبري فحص عشر ة أعمدة خفيفة190 ملم) وبطول ( 1000 ملم) والمعرضة الى احمال محورية × الوزن مربعة المقطع بابعاد ( 190ومقاومة الخرسانة للانضغاط . (lateral) لتقدير تاثير كمية الحديد الطولي وكمية الحديد العرضييمكن الملاحظة من خلال التجارب المختبرية (العملية) بان مادة ركام البورسل نايت جيدة انشائيا وملائمةلتنتج خرسانة خفيفة الوزن وكذلك يمكن الملاحظة عند الحفاظ على كمية الحديد الطولي ثابتة فانالزيادة في الحديد العرضي اربعة أضعاف حسب ماتحدده متطلبات الكود الامريكي لسنة 2005 يؤثرتاثيرا كبيرا على تصرف العمود في مرحلة ما بعد التشقق . ان تحسين اداء وكفاءة العمود من خلالاستخدام نسبة حديد عرضي اكبر يؤدي الى : أ-زيادة في المطيلية . ب-اقل تضررا لقلب العمودالخرساني (الجزء الخرساني من العمود والمحصور داخل الحديد العرضي). ج-زيادة 12 % للتحملالاقصى للعمود.كذلك تم تطوير معادلة تجريبية لحساب الحمل تاخذ بنظر الاعتبار تاثير الحديد العرضي.

Keywords

Porcelinite --- R.C. --- Columns


Article
Study of Linear Shrinkage for Siliceous Materials to Meet Insulating Requirements
دراسة التقلص الخطي للمواد السيليسية المحققة للمواصفة العازلية

Authors: Jubair, S.I شوكت إسماعيل جبير --- Kamis, R.A رعد عزاوي خميس --- Rassen, F.A فاضل عبد رسن
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2011 Volume: 9 Issue: 16 Pages: 73-78
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Iraqi siliceous rocks were chosen to be used as raw materials in this study which is concern with the linear shrinkage and their related parameters. They are porcelinite from Safra area (western desert) and Kaolin Duekla, their powders were mixed in certain percentage, to shape compacts and sintered. The study followed with thermal and chemical treatments, which are calcination and acid washing. The effects on final compact properties such as linear shrinkage were studied. Linear shrinkage was calculated for sintered compacts to study the effects of calcination processes, chemical washing, weight percentage, sintering processes, loading moment were studied on this property where the compacts for groups is insulating materials.Linear firing shrinkage test is very important in ceramic industries, when in some uses most be calculated the ceramic body volume before product.The results indicate that some of these groups satisfy ability the required linear firing shrinkage property for electrical insulator, so they are an ability to be used in industry.

يتضمن موضوع البحث اختيار نوع من الصخور السيليسية العراقية كمواد أولية وهي صخور البورسيلينايت من موقع الصفرة في الصحراء الغربية والكاؤولين العراقي (سيليكات) / دويخلة وخلط مساحيقهما بنسب وزنية معينة لتشكيل مكبوسات وتلبيدها ودراسة خواص التقلص الخطي وتأثير بعض العوامل المرتبطة بالعينات المشكلة من هذه المواد. تم إجراء معاملات حرارية (كلسنة) ومعاملات كيميائية (غسل بالحامض) للمواد الأولية ودراسة تأثيرها على الخواص النهائية للمكبوسات (التقلص الخطي). تم حساب التقلص الخطي للمكبوسات الملبدة والمحضرة من هذه الخلطات بهدف معاينة تأثير؛ عمليات الكلسنة والغسل الكيميائي وإضافة الكاؤولين وعمليات التلبيد ومقدار التحميل على تلك الخواص. علما أن هذه المكبوسات هي مادة عازلة أي أنها ناجحة في الفحص الحراري والكهربائي ويعد فحص التقلص الخطي وقياسه ذا أهمية بالغة في الصناعات السيرامكية حيث يتوجب في بعض الاستخدامات المعتمدة في الصناعات السيرامكية تحديد حجم الجسم السيراميكي المنتج وأبعاده قبل عملية تصنيعه، وبذلك إن النتائج تشير إلى إمكانية تشكيل نماذج صناعية من بعض الخلطات المختارة بالمواصفة المطلوبة في صناعة العوازل.


Article
Some properties of accelerated cured no fine Lightweight concrete
بعضخصائصالخرسانة خفیفة الوزن الخالیھ من الركام الناعم المعجلة الانضاج

Author: Zena K.A.Al Anbori زینة خضیر عباس
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 13 Part (A) Engineering Pages: 213-224
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Thermal insulation is one of the main problems facing the engineers working inbuilding and housing sector spatially for the high summer temperature in the mostArab Gulf and spatially in Iraq, so the study of lightweight aggregate thermalinsulation (No fine concrete) is important. The experimental work consist of concretemixes (cement: porcelinite aggregate) ratios (1:4), (1:5) and (1:6) and for each mixescement content changes (200, 300 and 400) Kg/m3. Dependence on mixing (1:5) andcement content (300Kg/m3) change the water to cement ratio (0.4, 0.45 and 0.5) byweight. The research presents the tests of density, absorption, porosity, ultrasonicpulse velocity, accelerated compressive strength according to British standard (BS1881: Part 112: 1983), normal compressive strength at 7, 28 and 90-day. Light weightconcrete was obtained of density ranging from (721-770) kg/m3 and thermalconductivity ranging from (0.17- 0.24) W/ (m.K). The good correlation betweenaccelerated compressive strength at one day with normal compressive strength at 28-day is approximately (0.245 ±0.005) for water bath at 55°C and (0.335±0.05) forwater bath at 82°C.


Article
Effect of Internal Curing on StrengthDevelopment of High Performance Concrete by Using Crushed Lightweight Porcelinite
تاثير الانضاج الداخلي على تطور المقاومة للخرسانة العالية الاداء وباستخدام البورسيلينايت المكسر الخفيف الوزن

Authors: Tareq S. Al-Attar --- Adil M. Abdullatif --- Ayman J. Al-Saad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 11 Part (A) Engineering Pages: 2803-2814
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

High performance concrete, HPC, requires a low water-to-cementitious materials mass ratio w/cm and supplemental cementitious materials with silica fumes in the mixture, and use of a superplasticizer. Because of the low w/cm and rapid reaction at early ages, it becomes more difficult to provide curing water from the top surface and this water will be inadequate to satisfy the conventional curing. Therefore, there is a need to use internal curing that is supplied via internal materials, such as absorbent lightweight aggregate, which will be pre-saturated. The use of internal curing was investigated in this study by two ways. The first way was through the use of partial replacement of original coarse aggregate (gravel), meanwhile, the second was by replacing partiallythe original fine aggregate (sand)by crushed Porcelinite.The results showed that the fine Porcelinite replacement as internal curing material caused better enhancement instrengthof HPC than coarse Porcelinite. The replacement of original fine crushed Porcelinite caused an increase in compressive strength from 3.36 to 5.25percent, for splitting tensile strength from 5.48 to6.85 percent and for flexural strength from 11.76 to 12.74percent.

الخرسانة العالية الاداء تتطلب كمية مياه قليلة نسبة الى المواد الاسمنتية مع اضافة مواد اسمنتية مثل السليكا فيوم الى الخليط واضافة المواد الملدنة الفائقة . بسبب قلة الماء الى المواد الاسمنتية وسرعة التفاعل في الاوقات المبكرة يصبح من الصعوبة انضاج الخرسانه من السطح الخارجي بالطرق التقليدية . لذلك نستخدم الانضاج الداخلي الذي يتم تطبيقه عن طريق مواد داخلية مثل الركام الخفيف ذو الامتصاص العالي ويستعمل كركام مسبق التشبع بالماء عند الخلط .في هذا البحث جرى دراسة تأثير الانضاج الداخلي علىالخواص الميكانيكية مثل المقاومة .تم اعتماد اسلوبين في انجاز الانضاج الداخلي وهما : استبدال جزئي للركام الخشن وبأستخدام حجر البورسيلينايت المكسر. وتم في الاسلوب الثاني استبدال جزئي للركام الناعم وايضا بأستخدام حجرالبورسيلينايت المكسر.اظهر البحث ان استبدال الركام الناعم لحجر البورسيلينايت المكسر كمادة أنضاج داخلي كان الافضل في تعزيز الخواص الميكانيكية (المقاومة) من استبدال الركام الخشن لحجر البورسيلينايت المكسر. وكمثال على ذلك فقد كان استبدال الركام الناعم الاصلي بمواد الانضاج الداخلي سببا في زيادة مقاومة الانضغاط بعمر 28 يوم وبمقدار يتراوح ما بين 3.36 و 5.25 في المائة . بينما لمقاومة الشد كانت الزيادة من 5.48 الى 6.85في المائة ومقاومة الانحناء كانت الزيادة تتراوح بين 11.76 الى 12.74 في المائة .


Article
NO-FINE LIGHTWEIGHT AGGREGATE CONCRETE MODIFIED WITH STYRENE BUTADIENE RUBBER
الخرسانة الخالية من الركام الناعم المصنوعة من الركام خفيف الوزن والمطورة بالبوليمر

Authors: Ali T. Jasim --- Qusay A. Jabal
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2010 Volume: 1 Issue: 2 Pages: 33-44
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

No-fines concrete is a form of lightweight concrete obtained when fine aggregate is omitted. No-fine concrete mainly used for both load bearing and non-load bearing for external walls and partitions and in in-filling panels in framed structures. The essential objective of this work is to investigate the effect of incorporation of polymer (SBR) on the performance of no-fine concrete made from lightweight aggregate (porcelinite) and to suggest possible applications of this type of concrete. Three concrete mixes with different aggregate/cement ratios (A/C) (6:1, 8:1 and 10:1) by volume were selected. Each of these mixes included six mixes which differed in polymer/cement ratios, (0%, 5%, 10%, 15% and 20%) by weight to find the optimum polymer/cement ratio. Density, compressive strength, splitting tensile strength and drying shrinkage were conducted on all concrete mixes. The test results showed that the compressive strength of no-fine lightweight aggregate concrete increased with the increase in polymer/cement ratio up to 15%, and the compressive strength reduced at polymer /cement ratio of 20% . At polymer/cement ratio of 15%, the percentage of increase in compressive strength measured relative to reference mixes was about 50%. On the other hand, the splitting tensile strength was increased with the increase in polymer/cement ratio for all mixes. The percentage of increase in splitting tensile strength compared with reference mixes increased from about 30 to 90% with the increase of polymer/cement ratio from 5 to 20 %. Also the drying shrinkage strains of no-fine concrete decrease, with the increase in polymer/cement ratio. The percentages of decrease in drying shrinkage strain at 56 days were from 5 to 30% with the increase of polymer/cement ratio from 5 to 20%.

تعد الخرسانة الخالية من الركام الناعم احد أنواع الخرسانة خفيفة الوزن حيث يتم ا لحصول عليها بحذف الركام الناعم من الخرسانة الاعتيادية. . ان الهدف الرئيسي من هذا البحث هو دراسة تأثير إضافة احد أنواع البوليمر المعروف باسم ستايرين بيوتادين على اداء الخرسانة الخالية من الركام الناعم والمصنوعة أيضا من الركام خفيف الوزن ومن ثم اقتراح التطبيقات المناسبة لهذا النوع من الخرسانة. تم استعمال ثلاث خلطات خرسانية بنسب مختلفة من الركام/ الاسمنت (( 10:1, 8:1 , 6:1 وكل خلطة من هذه الخلطات تضمنت نسب مختلفة من البوليمر/ الاسمنت (5 ,10 ,15 , و20%). بعد المعالجة الرطبة تم إجراء فحوصات الكثافة الجافة, مقاومة الانضغاط, مقاومة الشد الانشطاري, وانكماش الجفاف. أظهرت النتائج بان مقاومة الانضغاط تزداد بزيادة نسبة البوليمر/ الاسمنت ولغاية نسبة 15% بعد هذه النسبة تبدأ بالانخفاض إن نسبة الزيادة في مقاومة الانضغاط عند نسبة البوليمر/ الاسمنت 15% كانت تقريبا 50%. من جانب أخر إن مقاومة الشد الانشطاري تزداد بزيادة نسبة البوليمر/ الاسمنت حيث تراوحت الزيادة من 30 إلى 90% عند زيادة نسبة البوليمر/ الاسمنت من 5 إلى 20% . أشارت النتائج أيضا إن قيم انكماش الجفاف تنخفض بزيادة نسبة البوليمر/ الاسمنت حيث لوحظ بان نسبة الانخفاض بعمر 56 يوم تراوحت من 5 إلى 30% عند زيادة نسبة البوليمر/ الاسمنت من 5 إلى 20%.


Article
Performance of Fiber Light-Weight Aggregate Concrete Exposed to Elevated Temperatures
أداء الخرسانة خفيفة الوزن الحاوية على الألياف والمعرضة إلى درجات حرارة عالية

Authors: Shakir A. Salih --- Ali T. Jasim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 13 Pages: 2393-2410
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Two major problems arise when concrete is exposed to elevatedtemperatures. One is the deterioration in mechanical properties of concrete and the other problem is spalling of concrete. In recent times, the inclusion of polypropylene fibers had been reported to be a feasible method to prevent spalling of concrete subjected to elevated temperature. Additional problems arise due to the fact that by adding polypropylene fibers, the residual properties of heated concretemay be adversely affected. The essential objective of this work is to investigate the effect of incorporation of polypropylene fibers or/and steel fibers on the residual properties of lightweight concrete made from porcelinite aggregate after subjected to elevated temperatures. The concrete specimens heated to target temperatures of 100, 200, 400, 600 and 800 oC, at a rate of 10 oC per minute. When the targettemperature was reached, the specimens were kept at that temperature for 2 hours and then allowed to cool to room temperature by natural cooling. For each type of concrete, compressive strength, splitting tensile strength, static modulus of elasticity, and thermal expansion strains were determined before and after exposing the concrete to the target elevated temperatures. Experimental results indicated thatpolypropylene fiber-reinforced LWAC showed more reduction in its residual mechanical properties compared to plain LWAC. These different are more pronounced at exposure temperature of 200 and 400 oC. Average differences of 30,25 and 20 percent were observed in static modulus of elasticity, splitting tensile strength and compressive strength respectively, for specimens heated up to 400 oC. The addition of steel fibers inside the polypropylene fiber concrete would improvethe residual mechanical properties of heated concrete at temperature range 200 to 600 oC. On average, the improvement ranged from 9 to 20 percent.

هنالك مشكلتان رئيسيتان عند تعرض الخرسانة إلى درجات الحرارة العالية. المشكلة ألأولى هي تدهور الخواص الميكانيكية للخرسانة و المشكلة الأخرى هي تشظي الخرسانة. لقد وجد مؤخرا″ إن إضافة ألياف البولي بروبلين إلى الخرسانة هي طريقة مناسبة لمنع تشظي الخرسانة عند تعرضها إلى درجات الحرارة العالية. تظهر مشكلة أخرى نتيجة انصهار هذه الألياف حيثتوثر سلبا″ على خواص الخرسانة المعرضة للحرارة العالية. إن الغرض الرئيسي من هذا البحث هو التعرف على تأثير إضافة ألياف البولي بروبلين و/او ألياف الحديد على أداء الخرسانة خفيفة الوزن المنتجة من ركام البورسيلينايت بعد تعرضها إلى درجات الحرارة العالية. تم تسخين و بمعدل تسخين 10 o 600 و 800 م ,400 ,200 , النماذج الخراسانية إلى درجات حرارة 100 دقيقة وتم الإبقاء على درجة الحرارة المطلوبة لفترة ساعتين بعدها تم تبريدها بشكل طبيعي / o مإلى درجة حرارة الغرفة. تم في هذا البحث إجراء عدة فحوص تضمنت مقاومة الانضغاط, مقاومة الشد الانشطاري, معامل المرونة الساكن, والتمدد الحراري قبل وبعد تعرض النماذج إلى الحرارة العالية. سببت إضافة ألياف البولي بروبلين أكثر انخفاضا في الخواص الميكانيكية للخرسانة المسخنة مقارنة مع الخرسانة غير الحاوية على ألياف البولي بروبلين. هذا الانخفاض , حيث كان الاختلاف حوالي 30 o كان أكثر وضوحا عند درجات حرارة التعرض 200 و 400 م25 و 20 % في معامل المرونة الساكن, مقاومة الشد الانشطاري ومقاومة الانضغاط على أدت إضافة ألياف الحديد إلى الخرسانة الحاوية على . o التوالي للنماذج المسخنة لغاية 400 م ألياف البولي بروبلين إلى تحسين الخواص الميكانيكية للخرسانة المعرضة إلى درجات حرارة . % حيث كان معدل التحسن من 9 إلى 20 ,o 200 إلى 600


Article
The Effect of Different Types of Aggregate and Additives on the Properties of Self-Compacting Lightweight Concrete

Authors: Nada M. Fawzi --- Qusay Jar-Allah Hachim
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2012 Volume: 18 Issue: 8 Pages: 875-888
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The major aim of this research is study the effect of the type of lightweight aggregate (Porcelinite and Thermostone), type and ratio of the pozzolanic material(SF and HRM) and the use of different ratios of w/cm ratio(0.32 and 0.35) on the properties of SCLWC in the fresh and hardened state. SF and HRM are used in three percentage 5%,10%, and 15% as a partial replacement by weight of cement for all types of SCLWC. The requirements of self-compatibility for SCC are fulfilled by using the high performance superplasticizer (G51) at 1.2liter per 100 kg of cement. The values of air dry density and compressive strength at age of 28 days within the limits of structural lightweight concrete. The air dry density and compressive strength at age of 28 days for w/cm ratio(0.32) for SCLWC of Porcelinit aggregate are 1964 kg/m3 and 29.57 MPa, respectively. The corresponding values for the SCLWC of Thermostone aggregate are 1820 kg/m3 and 25.75 MPa, respectively. The results show that the HRM performance which is locally available is better than SF in production of SCLWC.

إن الهدف الرئيسي من البحث هو دراسة تأثير نوع الركام الخفيف الوزن(البورسيلينايت و الثرمستون) ونوع ونسبة المادة البوزولانية (الميتاكاوؤلين عالي الفعالية والسليكا فيوم) واستخدام نسبتين مختلفتين من نسبة الماء إلى الاسمنت(0.32 و 0.35 )على خواص الخرسانة خفيفة الوزن ذاتية الرص في الحالة الطرية والحالة الصلبة. استخدمت كل من السليكا فيوم والميتاكاؤولين عالي الفعالية بثلاث نسب 5%,10%,15% كاستبدال جزئي من وزن الاسمنت لكل نوع من أنواع الخرسانة خفيفة الوزن ذاتية الرص.وقد تم تحقيق متطلبات الخرسانة ذاتية الرص باستعمال الملدن عالي الأداء بنسبة 1.2لترلكل 100كغم من الاسمنت لكل نوع من أنواع الخرسانة خفيفة الوزن ذاتية الرص. كانت قيم الكثافة الجافة ومقاومة الانضغاط بعمر 28 يوم ضمن حدود الخرسانة الإنشائية خفيفة الوزن فالكثافة الجافة ومقاومة الانضغاط بعمر 28 يوم ولنسبة ماء إلى إسمنت تساوي 0.32 لخرسانة ذات ركام البورسيلينايت خفيف الوزن ذاتية الرص كانت 1964 كغمم3 و29.57 ميكاباسكال على التوالي بينما كانت في الخرسانة ذات ركام الثرمستون خفيف الوزن ذاتية الرص 1820 كغمم3 و 25.75 ميكاباسكال على التوالي وقد بينت النتائج بأن أداء الميتاكاؤولين عالي الفعالية المتوفر محليا أفضل من أداء المضاف( السليكا فيوم) في إنتاج الخرسانة خفيفة الوزن ذاتية الرص.


Article
Using of Porcelinite as Coarse Aggregate in Concrete
استخدام البورسلينات كركام خشن في الخرسانة

Author: Haifa M. Saleh
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2012 Volume: 19 Issue: 3 Pages: 33-40
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

In this research the ability of using porcelinite as coarse aggregate to produce light weight concrete was investigated. The experimental program consists of preparing and testing a mixes to investigate mechanical properties of concrete, with a total of 15 cubes (100×100×100) mm, 30 cylinders (100×200) mm. The tests include compressive strength, splitting tensile strength, fresh and hardened density of light weight concrete for different porcelinite percentages ranged between(0% to 100%) of the coarse aggregate weight. The obtained results for tested specimens were compared to control one. Test results indicated that using of porcelinite in concrete mix reduces the strength of concrete Porcelinite aggregate represents a reduction in density ranging between (10%-36%) of normal weight concrete, therefore there is an advantage using this type of light weight aggregate in this country where soil bearing capacity is low in most construction sites.


Article
Some Mechanical Properties of Concrete by using Manufactured Blended Cement with Grinded Local Rocks
بعض الخواص الميكانيكية للخرسانة الحاوية على سمنت مخلوط مع مطحون صخور محلية

Authors: Zena K. Abbas Al-Anbori زينة خضير عباس العنبوري --- Ahmed A. Ibrahim Al-Obaidi احمد علي ابراهيم العبيدي
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2016 Volume: 22 Issue: 3 Pages: 1-21
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The use of blended cement in concrete provides economic, energy savings, and ecological benefits, and also provides. Improvement in the properties of materials incorporating blended cements. The major aim of this investigation is to develop blended cement technology using grinded local rocks . The research includes information on constituent materials, manufacturing processes and performance characteristics of blended cements made with replacement (10 and 20) % of grinded local rocks (limestone, quartzite and porcelinite) from cement.The main conclusion of this study was that all types of manufactured blended cement conformed to the specification according to ASTM C595-12 (chemical and physical requirements). The percentage of the compressive strength for blended cement with 10% replacement are (20, 11 and 5) % , (2 , 12 and, 13) % and (18, 15 and 16) % for limestone , quartzite and porcelinite respectively at (7,28 and 90)days for each compare to the reference mix, while blended cement with 20% replacement are (-3, -5 and -11) ,(6, -4% and -5) and (6, 4 and 6) % for limestone , quartzite and porcelinite respectively at (7, 28 and 90)days compare to the reference mix .The other mechanical properties (flexural tensile strength and splitting tensile strength) are the same phenomena of increase and decrease in compressive strength. The results indicated that the manufacture Portland-limestone cement, Portland-quartzite cement and Portland-porcelinite cement with 10% replacement of cement with improvable mechanical properties while the manufacture Portland-porcelinite cement with 20% replacement of cement with slight improvable mechanical properties and more economical cost.

استخدام السمنت المخلوط في الخرسانة يوفر اقتصاديا, حفظ للطاقة , الفوائد البيئية و كذلك يوفر تحسنا في خواص المواد التي يستخدم فيها السمنت مخلوط. الهدف الرئيسي من هذا البحث هو تطوير سمنت مخلوط من مطحون الصخور المحلية , البحث يتضمن معلومات عن عملية الخلط والتصنيع وخصائص الاداء مع نسب الاستبدال (10 و20)% من مطحون الصخور المحلية (الحجر الجيري , الكوارتزايت و البورسلينايت ) من السمنت . الاستنتاج الرئيسي من هذه الدراسة هو ان جميع انواع السمنت المخلوط المصنع مطابق للمواصفة الامريكية ASTM C595-12 للمتطلبات الفيزيائية والكيميائية الخاصة بالسمنت المخلوط .نسبة نتائج فحص مقاومة الانضغاط للخرسانة الحاوية على 10 % استبدال من السمنت هي كالاتي (5,11,20)% , (13,12,2)% و (16,15,18)% للحجر الجيري , الكوارتزايت والبورسلينايت على التوالي في (90,28,7) يوم لكل نوع مقارنه بالخلطه المرجعيه , في حين ان الاستبدال مع 20 % من السمنت هي كالاتي (-3,-5,-11)%, (6,-4,-5)% و(6,4,6) للحجر الجيري , الكوارتزايت والبورسلينايت على التوالي في (90,28,7 ) يوم. اما الخواص الاخرى (فحص قوة الانثناء ,فحص قوة الانشطار) فمن خلال النتائج يتبين ان الزيادة والنقصان هي في الاتجاه ذاته في فحص مقاومة الانضغاط. النتائج توضح ان افضل نسبة استبدال من السمنت من مطحون (الحجر الجيري , الكوارتزايت و البورسلينايت ) هي نسبة 10% مع تحسن جيد بينما يمكن أستخدام 20% لمطحون البورسلينايت مع تحسن طفيف للخواص الميكانية و أقل كلفة .


Article
EXPERIMENTAL STUDY FOR THE SIZE EFFECT ON THE FLEXURAL BEHAVIOUR OF SPLWA REINFORCED CONCRETE SLABS STRENGTHENED WITH CFRP STRIPS
دراسة عملية لتأثير الحجم على تصرف الانحناء للبلاطات الخرسانية المسلحة الخفيفة والمقواة بشرائح البوليمر المسلحة بألياف الكربون

Author: رياض عبد الرضا الغرة
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2014 Volume: 3 Issue: 1 Pages: 60-74
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

An experimental Study was conducted to investigate the size effect on the flexural behaviour of sand-porcelinite lightweight aggregate reinforced concrete one way slabs (SPLWAC OWS). In order to get a clear results, eight slabs were casted, and six of them were strengthened with carbon fibre reinforced polymer (CFRP) strips. To investigate the size effect, four slabs were of 300 mm width, 1500 mm length and 80 mm depth and the others were of 300mm width, 2000 mm length and 108 mm depth. The present study showed that the SPLWAC OWS showed a reverse size effect. The failure mode was by yield of steel for the control un-strengthened slabs, while it was by yield of steel followed by rupture of CFRP strips for the strengthened slabs. Also, the results of this study were compared with those obtained by the ACI equations. This comparison showed that the ultimate moment strength and deflection obtained by the ACI equations were always less than those obtained experimentally.

يقدم هذا البحث دراسة عملية لتأثير الحجم على سلوك الانحناء للبلاطات الخرسانية المسلحة الخفيفة. لغرض انجاز البحث، تم تحضير ثمان بلاطات، ستة منها مقواة بشرائح البوليمر المسلحة بألياف الكربون. لدراسة تأثير الحجم تم تحضير اربع بلاطات بأبعاد 300 ملم عرض، 1500ملم طول و 80 ملم سمك وأربع بلاطات بأبعاد 300 ملم عرض، 200 ملم طول و 108 ملم سمك . أظهرت هذه الدراسة تأثير عكسي للحجم على تصرف الانحناء للبلاطات. كانت طبيعة الفشل بواسطة خضوع حديد التسليح في البلاطات غير المقواة، بينما كانت طبيعة الفشل بواسطة خضوع حديد التسليح يتبعه تمزق شرائح البوليمر في البلاطات المقواة. تم مقارنة نتائج هذه الدراسة مع معادلات الكود الأمريكي وأظهرت المقارنة أن تحمل العزم الأقصى والهطول المحسوب باستخدام معادلات الكود الأمريكي كانت دائما اقل من نتائج الدراسة العملية.

Listing 1 - 10 of 12 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (12)


Language

English (9)

Arabic (2)

Arabic and English (1)


Year
From To Submit

2016 (1)

2014 (2)

2013 (2)

2012 (2)

2011 (1)

More...