A Sandwich Porous Alumina Nanostructures Based on Anodic Alumina
التركيب النانوي لشطيرة الألومينا المسامية المبنية على أنودة الألومينا

Authors: Zeinab A. Jawad --- Ahmed A. Moosa --- Abdul Qader D. Faisal
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 11 Pages: 2091-2102
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

A sandwich porous anodic alumina membrane (PAA/Al/PAA) films was producedusing two-step anodization approach on both sides of (250) μm pure aluminum foilelectrode as an anode. A single sheet of stainless steel or graphite was used as acathode. Anodization on both sides of aluminum sheet was achieved. The anodizationprocesses and pore formation were studied and discussed in this work. The producedalumina membrane (5-30) μm thick was analyzed using scanning electron microscopy(SEM). The SEM image shows the PAA membranes has a well-defined nanostructure.The average pore diameter reaches (25) nm. The produced Al 2O3 membrane growingon both sides of aluminum sheet was separated into a twin nano membrane.

تم انتاج أغشية من الألومينا المسامي بطريقة الأنودة وبشكل الشطيرةباستعمال طريقة الأنودة ذات المرحلتين وعلى الجهتين لقطب من صفيحة (PAA/Al/PAA)الألمنيوم النقي بسمك 250 مايكروميتر كقطب الأنود.أُستعلمت صفيحة مفردة من الفولاذ اوالكرافايت كقطب الكاثود. تم أجراء الأنودة على الجهتين لصفيحة الألمنيوم. درس في هذا البحث(30- عمليات الأنودة وتكوين المسامات. تم تحليل أغشية الألومينا المنتجة ذات سمك حوالي ( 5(PAA) أظهرت النتائج بأن الأغشية .(SEM) مايكروميتر باستعمال المجهر الألكتروني الماسحتمتلك تركيب نانوي. ان معدل القطر المسامي يصل الى 25 نانوميتر. ان الغشاء المنتج للألومين اعلى جهتي صفيحة الألمنيوم قد تم فصله الى غشائين ذا تركيب نانوي.

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

English (1)


Year
From To Submit

2010 (1)