Study the Effect of Addition Different Amount Magnesium Hydroxide and Kaolin on Production of Refractory Magnesite Brick
دراسة تأثير اضافة نسب مختلفة من هيدروكسيد المغنسيوم ومادة الكاؤولين على تصنيع الطابوق الحراري المغنيسي

Authors: Firas Farhan Sayyid فراس فرحان سيد --- Shukry H. Aghdeab شكري حميد غضيب --- Ali Mundher Mustafa علي منذر مصطفى
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 13 Part (A) Engineering Pages: 546-553
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This aim of this research is study the effect of adding different percentages of magnesium hydroxide, kaolin and water on the production of refractory magnesite brick by use transformer process. Firstly transformative process carried out on the magnesium hydroxide and kaolin to obtain fine particle, after that mixture fine particle Burn in electric furnace at temperature (1000 oC ) for (2 hr ). The mixture Formed by using semi dry pressing with (10)% water under pressure (500 Kg/cm2) to obtain forming sample we carried out drying process ,and we can many test from inspection for obtain porosity, density, Water absorption, specific weight and more properties compressive strength . We fined finish refractory brick from light type where the resulted density is equal to ( 1.33 gcm3 ) and suits applications that need to lightness weight with durability.

يهدف هذا البحث الى دراسة تاثيراضافة نسب مختلفة من مادة هيدروكسيد المغنسيوم ومادة الكاؤولين والماء على تصنيع الطابوق الحراري ، تم اولآ اجراء عملية تحويلية على مادة هيدروكسيد المغنسيوم ومادة الكاؤولين لغرض الحصول على حبيبات ناعمة ، حيث اجريت عملية حرق لخليط من هيدروكسيد المغنسيوم و الكاؤولين في فرن كهربائي لغاية درجة حرارة (1000 oC ) ولمدة ساعتين . بعدها تم تشكيل الخليط بطريقة الكبس شبه الرطب وذلك بأضافة (10 )% من الماء وتحت ضغط 500 Kgcm2 ) ) للحصول على النماذج مشكلة نتبعها باجراءعملية تجفيف للنماذج النهائية . اجريت مجموعة من الفحوصات لتحديد المسامية ،الكثافة,امتصاص الماء,والوزن النوعي ومقاومة الانضغاط . حيث وجد ان الطابوق الحراري الذي تم الحصول علية هو من النوع الخفيف و ان الكثافة التي تم الحصول عليها هي ( 1.33 gcm3 ) ويلائم التطبيقات التي تحتاج الى خفة وزن مع متانه .


Article
Iraqi Bauxite and Porcalinite Rocks Based Refractory, Preparation and Studying Properties
الخصائص الفيزيائية والحرارية لحراريات مصنعة من صخور البوكسايت والبورسلينات العراقية

Author: Amel S. Merzah امل صالح مرزة
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2017 Volume: 13 Issue: 2 Pages: 70-78
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Locally natural occurring Iraqi rocks of Bauxite and Porcelanite (after pre calcinations at 1000oC for 1hr) were used, with the addition of different proportions of MgO and Al2O3, to prepare refractory materials. The effects of these additives on the physical and thermal properties of the prepared refractories were investigated.Many batches of Bauxite/MgO, Bauxite/Al2O3, Bauxite/MgO/Al2O3, and Porcelanite/ MgO/Al2O3 were prepared. The mixture is milled and classified into different size fractions; fine (less than 45μm) 40%, middle (45-75μm) 40%, and coarse (75-106μm) 20% . X-ray diffraction technique was used to identify the structure of Bauxite and Porcelanite rocks. The samples were formed by semi dry pressing with the addition of few drops of water as a binder. These samples were sintered at 1100oC for 2hrs. Physical properties (linear shrinkage, density and porosity), and the thermal properties (thermal conductivity, diffusivity and specific heat) were measured for all the prepared samples. The results show the increasing of density is susceptible to the thermal properties, and also the addition of Al2O3 and MgO to the natural rocks have a limited effect, and the values of the parameters above for the natural rocks, were in the levels to be used as a refractory material for lining a metal fusion furnaces and other applications.

الصخور المحلية الموجودة طبيعيا في العراق (البوكسايت والبورسلينات) والمحروقة اوليآ بدرجة حرارة 1000درجة مئوية ولمدة ساعة واحدة, تم استخدامها لتحضير حراريات وبإضافة نسب مختلفة من المغنيسيا والالومينا .تم فحص تأثير هذه الاضافات على الخصائص الفيزياوية والحرارية للحراريات المحضرة.تم تحضير وجبات عديدة من البوكسايت/ مغنيسيا, البوكسايت/ الومينا, البوكسايت/ مغنيسيا/ الومينا وايضآ تم تحضير وجبات أخرى للبورسلينات/ مغنيسيا/ الومينا وبنسب مختلفة . تم طحن المزيج وتصنيفه بحسب الأحجام والكسور الحجمية الى ( اقل من 45 مايكرون )40% , والوسط ( 45 -75) 40% , والخشنة (75 – 106) 20%.استخدمت تقنية حيود الاشعة السينية للتعرف على تركيب الصخور. و تم تشكيل النماذج باستخدام الكبس شبه الجاف بإضافة قطرات قليلة من الماء بوصفها مادة رابطة . هذه النماذج تم تلبيدها بدرجة حرارة 1100 درجة مئوية لمدة ساعتين . الخصائص الفيزيائية (الانكماش الخطي, الكثافة, والمسامية), والخصائص الحرارية (التوصيلية الحرارية, الانتشارية, والحرارة النوعية), تم قياسها لكل النماذج المحضرة .أثبتت النتائج إن الكثافة تتأثر بالخصائص الحرارية , وان إضافة الالومينا والمغنيسيا للصخور الطبيعية لها تأثير محدود .وقيمة العوامل المذكورة أعلاه لهذه الصخور الطبيعية هي بالمستويات التي تؤهلها للاستخدام بوصفها حراريات لتبطين أفران صهر المعادن وتطبيقات أخرى.