Synthesis of Nanosilica Glass Activated by Erbium Ions, Spectroscopic studies
توليف زجاج النانو سليكا المطعم بايونات الاربيوم، دراسات طيفية

Loading...
Loading...
Abstract

Erbium, as optical probe, doped silicate sol-gel glass with different Er concentrations was formed by wet chemical synthesis method using ethanol, water and tetraethaylorthosilicate [Si(OC2H5)4] precursor. Erbium ions were incorporated into silica sol-gel matrix via dissolution of Erbium chloride solution into the initial Si(OC2H5)4 precursor sol. Aluminum (Al) as a co-dopant was added to the final precursor in the form of Aluminum chloride (AlCl3) solution. The prepared samples were analyzed using atomic absorption analysis, X-ray diffraction and spectroscopic tests. The experimental results concerned with the transmission spectra suggest that the final samples have a good transparency and homogeneity. Also, the X-ray diffraction test showed that they have amorphous structure. The absorption and fluorescence spectra, as a function of Er concentration, were recorded at room temperature. Fluorescence emission of the 4I13/2→4I15/2 transition at ~ 1.536 µm was observed. In addition, the high values of peak emission cross-section, which were calculated as a function of Er concentration, suggest that the Er in the sol-gel may be favorable as optical material

الاربيوم كمجس بصري تم تطعيمه بزجاج السيليكات Sol-gel وبتراكيز مختلفة بأستخدام الطريقة الكيميائية الرطبة بأستعمال كحول الايثانول, الماء و محلول التتراثيل اورثو سيليكات [Si(OC2H5)4]. ايونات الاربيوم تداخل في مصفوفة السيليكا بواسطة اذابة محلول كلوريد الاربيوم في محلول [Si(OC2H5)4] الاولي. الالمنيوم كشائب مشارك قد تم اضافته الى المحلول النهائي بصيغة محلول كلوريد الالمنيوم.حللت النماذج المحضرة باستخدام تحليل الامتصاص الذري، حيود الاشعة السينية بالاضافة الى الفحوصات الطيفية. اظهرت النتائج التجريبية المتعلقة باطياف النفاذية امتلاك النماذج المحضرة لنفاذية وتجانس جيدين، كذلك اظهرت اطياف حيود الاشعة السينية التركيب العشوائي لهذة النماذج.سجلت اطياف الامتصاص والفلورة للنماذج كدالة لتركيز ايون الاربيوم عند درجة حرارة الغرفة وقد لوحظ انبعاث الفلورة الخاص بالانتقال 4I13/2 4I15/2 عند تقريبا 1.536μm. اضافة الى ذلك فان القيم العالية لذروة المقطع العرضي للانبعاث والتي حسبت كدالة لتركيز ايون الاربيوم بينت أن الاربيوم المطعم بزجاج الـ Sol-gel قد يكون مفضلا كمادة بصرية ليزرية.

Keywords

Erbium --- silica sol-gel


Article
Study the spectroscopy of samarium encapsulated in silica Xerogel matrices
دراسة مطيافية السماريوم المغلف بمصفوفات السيليكا Xerogel

Loading...
Loading...
Abstract

The sol-gel preparation technique of transparent silica monoliths containing up to 0.5 M of samarium have been described. The sol-gel processing parameters are: acid catalyzed hydrolysis and controlled drying. The prepared monoliths are analyzed by X-ray diffraction, pycnometer measurements, Fourier transformation infrared spectroscopy and optical spectroscopy. The oscillator strengths of the Sm3+ ions in the silica monoliths are calculated. The results show a linear concentration dependence of some Sm3+ transitions in UV/Vis absorption spectra and formation of Sm3+ clusters inside the pores structure of silica monoliths at high Sm3+ concentration.

تم وصف تقانة ال Sol-Gel لتحضير كتل حجمية من السيليكا الشفافة المطعمة بتراكيز مختلفة لغاية 0.5 تركيز مولاري من ايونات السماريوم. ان المتغيرات الخاصة بعملية ال Sol-Gel كانت: العامل المساعد الحامضي لعملية الهدرجة والسيطرة على عملية التجفيف. تم تحليل نماذج الكتل الحجمية المحضرة باستخدام حيود الاشعة السينية, قياسات الكثافة, مطيافية الاشعة تحت الحمراء و المطيافية البصرية. تم حساب شدة التذبذب لانتقالات ايونات السماريوم في نماذج السيليكا الحجمية. لقد أظهرت النتائج وجود اعتماد خطي لقمة حزم بعض انتقالات ايون السماريوم مع التركيز ضمن المدى الطيفي الفوق بنفسجي/ مرئي, كذلك أظهرت النتائج تشكل مجاميع من ايونات السماريوم داخل المسامات التركيبية لنماذج السيليكا الحجمية عند التراكيز العالية للسماريوم.