Article
Comparison of Applied Pressure Effect on ImprovingDensity, Hardness, and Microstructure by Both SqueezeCasting Process and Pressure Die Casting Process for 380-Al Alloy

Author: Dr. Najeeb S. Abtan Dr. Kadhim H. Ghlaim
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2012 Volume: 12 Issue: 2 Pages: 334-344
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The present study includes the effect of applied pressure on elimination theporosities that formed during both squeeze casting process and pressure die casting.For pressure die casting the pressure was applied on the full liquid molten alloy (750oC) where the pressure was applied on molten alloy at (650oC) i.e. the molten was fifty liquid fifty solid (mushy zone). The tests and measurements of density, hardness, and microstructure show theimprovement in density and hardness for the samples of both techniques but theincreasing in hardness and density values in squeeze casting were higher than thevalues of pressure die casting samples also the test of microstructure shows thedecreasing in (DAS) for the squeeze sample more than the (DAS) of pressure castingsamples.The above improvement in microstructure, hardness, density belongs to the behaviorof applied pressure in both cases which means that the mushy zone of molten alloyrepresents the optimum region to improve the mechanical properties by appliedpressure


Article
The Effect of Ceramic Particale Oxides addition on Wear Resistance of Composite Material for Aluminum Base Alloy
تأثير اضافة دقائق أوكسيدية سيراميكية على مقاومة البلى لمادة متراكبة ذات أساس من سبيكةألالمنيوم

Authors: Israa Abdulkader --- Maryam Abduladhem
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 7 Pages: 1249-1264
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

To The aim of this research is to study the effect of 5 wt % Al2O3addition Al- base alloy on sliding wear resistance under dry slidingconditions using pin- on- disc machine . Wear test was conductedafter squeeze casting under different pressure ( 30 , 60 , 90) Mpa.The results show that wear rate for Al- base alloy compositesincreases with increasing applied load but decreases with increasingsliding speed conditions . The composites which casting at 90 Mpapressure represents lower wear rate than those which cast at 30, 60 Mpapressure and the base alloy . The results also observed that thecoefficient of friction increasing with increasing sliding time but reaches to the steady state after 200 sec. The microhardness and ultimate tensile strength increases with increasing squeeze casting pressure.

يهدف هذا البحث الى دراسة تأثير أضافة دقائق أوكسيد ألالمنيوم بنسبة مئوية وزنية 5 % لسبيكة ذات اساس المنيوم على مقاومة البلى الانزلاقي تحت ظروف الانزلاق الجاف باستخدام جهاز ذو ترتيبة المسمار على القرص . لقد تم اجراء اختبار البلى بعد اجراء السباكة . ( 90 . 60 ، 30 ) Mpa بالعصر تحت ضغوط عصر مختلفة تبين من النتائج ان معدل البلى للسبيكة الاساس والمادة المتراكبة يزداد مع ازدياد الحمل المسلط لكنه يقل مع ازدياد سرعة الانزلاق . كما تبين ان المادة المتراكبة الناتجة بعد اجراء 90 اظهرت معدل بليان منخفض مقارنة مع المادة Mpa سباكة العصر تحت ضغط 60 و 30 ) والسبيكة الاساس . كما اظهرت النتائج ان ) Mpa المتراكبة المسبوكة تحت ضغط معامل الاحتكاك يزداد مع ازدياد زمن الانزلاق ثم يصل الى حالة الاستقرار بعد مرور 200ثانية من الاختبار . أما بالنسبة لقيم الصلادة الدقيقة ومقاومة الشد القصوى فانها تزداد مع ازدياد ضغط السباكة بالعصر.


Article
Study of Dry Sliding Wear Behavior of Al-12%Si alloy Produced By Squeeze Casting
دراسة سلوك البلى الأنزلاقي الجاف لسبيكة الألمنيوم-12 %سليكون المنتجة يطريقة السباكة بالعصر

Loading...
Loading...
Abstract

The present research deals with study of the effect of applied casting pressure at constant pouring and die preheating temperatures on the microstructure and dry sliding wear behavior of the squeeze cast Al-12%Si alloy was investigated. A pin-on-disc tests were conducted at varying loads from 5 to 20 N and a sliding speed of 2.7m/sec for a constant sliding time of 20min. The results showed that a refinement in the microstructure with increasing the squeeze pressure. The results showed that the wear rates and coefficient of friction ( μ ) of the squeeze cast samples are lower than that of the gravity die cast sample. The results also showed that the density of the specimens decreased with application of a 7.5 MPa applied pressure, but it increased steadily for higher pressures up to 53 MPa. Increasing the squeeze pressure resulted in increasing the hardness and decreasing the wear rate. These results were explained based on the densification mechanism brought about by the application of pressure during solidification.

يتناول هذا البحث دراسة تاثير ضغط السباكة المسلط عند درجات حرارة صب وتسخين مسبق لقالب الصب ثابتة على التركيب المجهري وسلوك البلى الأنزلاثي الجاف لسبيكة الالمنيوم –12% سليكون المنتجة بطريقة السباكة بالعصر. وأجريت أختبارات البلى من نوع المسمار على القرص عند أحمال متغيرة من 5 -20 نيوتن وسرعة أنزلاق 2.7 متر/ثانية ولفترة زمنية ثابتة 20.دقيقة. واظهرت النتائج حصول تنعيم في البنية المجهرية مع زيادة ضغط السباكة. اظهرت النتائج أن معدلات البلى ومعامل الأحتكاك ( μ ) للنماذج المنتجة بطريقة السباكة بالعصرأقل مما هو عليه في حالة النموذج المنتج يطريقة السباكة بالجاذبية. واظهرت النتائج ايضا بان كثافة العينات قد قلت عند تطبيق ضغط مسلط مقداره (7.5MPa), لكنها قد زادت بصورة ثابتة عند تسليط ضغوط اعلى الى حد (53MPa). ان زيادة ضغط السباكة ادت الى زيادة الصلادة وتقليل معدل البلى. ان هذه النتائج قد تم تفسيرها بالاعتماد على الية زيادة الكثافة الناتجة بواسطة تطبيق الضغط اثناء التجمد.


Article
Effect of Yttria Content up to 15wt% on Mechanical Properties of Al-Y2O3 Composites Prepared Via Squeeze Casting and Powder Metallurgy Routes
تأثير محتوى اليتيريا لغاية 15 wt % على الخواص الميكانيكية لمتراكبات Al-Y2O3 المحضرة عن طريق السباكة بالعصر وتقانة ميتالورجيا المساحيق

Authors: Farouk M. Mahdi فاروق منصور مهذي --- Abd-Ulkader A. Annaz عبذالقادر أحمذ عناز
Journal: Sulaimania Journal for Engineering Sciences مجلة السليمانية للعلوم الهندسية ISSN: 24101699/24156655 Year: 2015 Volume: 2 Issue: 2 Pages: 55-64
Publisher: university of Sulaimania جامعة السليمانية

Loading...
Loading...
Abstract

In this study Al - (0-15 wt %) Y2O3 composites were prepared by both squeeze casting and powder metallurgy routes. It was found throughout this work that Vickers microhardness, compressive yield strength and wear resistance increase continuously with increasing Yttria content up to 15wt% despite the preparing method. Powder metallurgy composites showed higher hardness and compressive strength compared with those of squeeze casting. On the other hand, both squeeze casting, at squeeze pressure of 15 and 20 MPa, and powder metallurgy routes gave approximate wear rates except that of pure aluminum where squeeze casting specimens showed much lower wear rates than those of powder metallurgy. It was also found that squeeze pressure has great effect on grain refining and Chinese script microstructure evolution. XRD patterns reveal high level of harmful oxides and intermetallic compounds in squeeze casting composites as compared with those prepared by powder metallurgy technique.


Article
STUDY OF DRY SLIDING WEAR RESISTANCE OF COMPOSITE MATERIALS OF AN ALLOY(AL – 12 % SI) REINFORCED WITH SIC PARTICLES
دراسةمقاومة البلى الانزلاقي الجاف لسبيكة معدنية ذات اساس من سبيكة الالمنيوم 12% سليكون مقواة بدقائق كاربيد السليكون

Author: Husein M. Habeeb حسين موسى حبيب
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2011 Volume: 11 Issue: 1 Pages: 172-181
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

AbstractIn this study, composite materials of an aluminum alloy(Al – 12 % Si) matrix reinforced with 5wt% SiC particles were prepared by gravity die casting and squeeze casting under casting pressure of ( 38MPa) and mold preheating at temperature (200 oC).Microstructure and hardness for prepared base alloy and composite materials were carried ou. Dry sliding wear type (pin–on-Disc) with variation in applied load was carried out under a constant steel hardness (35 HRC), sliding speed (2.7 m / sec) and sliding time (20 min).It has been found that prepared base alloy(Al – 12 % Si) and composite materials produced by squeeze casting have wear resistance better than that of base alloy and composite materials produced by gravity die casting.

موينمللأا ةكيبس نم ساسأ تاذ ةبكرم داوم ريضحت مت(Al – 12 % Si) ةاوقم ةبسنب نوكيلسلا ديبراك قئاقدبةينزو (%5) رصعلاب هكابسلاو ةيبذاجلاب هكابسلا نيتقيرطبو سبك طغض ريثأت تحت(38MPa) ةرارح هجرد دنع بلاقلل ىلوأ نيخستو 200مo.رابتخأ يرجأ كلذكو هجتنملا ةبكرملا داوملل هدلاصلاو يرهجملا صحفلا تارابتخأ تيرجأيقلازنلأا ىلبلا صرقلا ىلع رامسملا عون فاجلا (pin – on – Disc) مع تغير الحمل2.7 ) وزمن m / sec) 35 ) وسرعة الأنزلاق HRC) المسلط وثبوت صلادة القرص.(20 min) الأنزلاقساسلأا ةكيبسلا نإ ىلإ والمواد المركبة المنتجه بطريقه (A1 – 12% Si) وتم التوصيلالسباكه بالعصر ذات مقاومة بلى أعلى مما هو عليهِ في حالة السبيكة الأساس والموادالمركيةالمنتجه بالسباكة بالجاذبيه.


Article
OPTI MIZATION OF THE SQUEEZE CAST Y2O3/Al-Si COMPOSITES BY MERIT RATING METHOD
امثلية متراكبات Y2O3/Al-Siالمحضرة بواسطة السباكة بالعصر

Author: Osama Sultan Muhammed
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2011 Volume: 11 Issue: 3 Pages: 466-474
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

ABSTRACTIn this paper, Y2O3/Al–Si composites are prepared by squeeze casting process andmerit rating method is used to optimize the squeeze casting process parameters. Awear rate and hardness tests were conducted and the density is calculated for theresulted castings. The primary objective is to use merit rating method to find a bettergroup of parameters that give the good balance of high density and hardness with lowwear rate. The evaluated squeeze casting parameters are pouring temperature, dietemperature, and squeeze pressure. The experimental and analytical results showedthat the merit rating method was successful in determining the group of parametersthat give an optimum balance of properties. Also it showed that if the difference inany property values among specimens is high, it can affect the selection process withthe importance sequence.

ابعملية السباكة بالعصر وتم استخدام طريقة التقييم Y2O3/Al-Si تم في هذا البحث تحضير مت ا ركباتالمستحق لايجاد امثلية متغي ا رت عملية السباكة بالعصر. تم اج ا رء فحوصات معدل البلى والصلادة وحسابالكثافة للمسبوكات الناتجة. ان الهدف الاساسي هو استخدام طريقة التقييم المستحق لايجاد المجموعة الاحسنمن المتغي ا رت التي تعطي التوازن الجيد من الكثافة والصلادة العالية مع معدل البلى القليل للمسبوكات. متغي ا رتعملية السباكة بالعصر المقيمّة هي درجة ح ا ررة الصب، درجة ح ا ررة القالب وضغط العصر. اظهرت النتائجالتجريبية والتحليلية ان طريقة التقييم المستحق كانت ناجحة في تقييم وايجاد مجموعة المتغي ا رت التي اعطتالتوازن الامثل للخواص. اظهرت كذلك انه اذا كان الاختلاف في قيم اي خاصية بين العينات عاليا فانه يمكنان يؤثر على عملية الاختيار مع تتابع الاهمية


Article
Study the Effects of Squeeze Casting Parameters on the Corrosion Behavior of Al-Si-4Cu Alloy

Authors: Rabiha S. Yaseen --- Hussein A. Hussein --- Amjad H. Jassim
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 3 Pages: 558-570
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This study investigated the effects of squeeze parameters on the properties of squeeze castings and the optimum parameters for producing squeeze castings from Al-Si alloy. It also compared the properties of the squeeze castings with those of gravity castings. Squeeze castings were made from Al-Si-4Cu alloy using pressures of 10,15,20,25 and 30 MPa with the alloy poured at 750, 800 and 850oC into a die preheated to 300oC. Squeeze time was 30s. The corrosion experiments were performed over a range of elevated pressure, pouring temperature and were carried out in sea water (3.5% NaCl solution). We have focused to determination of the rate of corrosion and other corrosion characteristics. Both as-gravity cast and squeeze specimens were tested, for comparison. Corrosion behavior of the materials was assessed by the corrosion potential by potentiostate (polarization) curves. It was found that for a specific pouring temperature,microstructure of squeeze castings became finer;mechanical properties were increased with increase in pressure to their maximum values. Compared with gravity casting process, squeeze casting enhanced the mechanical properties; it increased the hardness from Hv 18.083 Kg for gravity castings to a maximum of Hv 35.413 for squeeze castings which constitutes about 50.063% increase over those of gravity castings. Although squeeze casting parameter has decreased the corrosion current density (of about 2 μAcm2) when compared to the results of the as-cast samples

في هذا البحث تم دراسة متغيرات السباكة بالعصر على خواص المسبوكات لتحديد المتغيرات المثلى لانتاج سبيكة المنيوم نحاس سليكون وكذلك مقارنة خواص السباكة بالعصر مع خواص السباكة التقليدية. المتغيرات المستخدمة في سباكة العصر لسبيكة الالمنيوم نحاس سليكون, الضغط المستخدم 30,25,20,15,10 Mpa ودرجة حرارة صب 850,800,750 درجة مئوية, مع تسخين مسبق للقالب الى cº300 وزمن الضغط 30 ثانية. استخدمت تجارب التاكل في ماء البحر بتركيز 3.5% NaCl. تم حساب سلوك التاكل للسبيكة بواسطة المجهاد الساكن (منحنيات الاستقطاب) حيث وجد ان الخواص الميكانيكية ومقاومة التاكل تزداد مع زيادة درجة حرارة الصب والضغط, حيث اصبحت البنية المجهرية دقيقة وازدادت الخواص الميكانيكية مقارنتا بالسباعة التقليدية. حيث ان صلادة فيكرز 18.083 للسبيكة التقليدية و 35.413 للسباكة بالعصر, الزيادة تقريبا 50.63 حيث ان متغيرات السباكة بالعصر قللت كثافة تيار التاكل 2 mAp مقارنة بالسباكة التقليدية.


Article
Evaluation Of Future Performance of Northern Fatha Storage System
دراسة تأثير الضغط المسلط على البنية المجهرية والكثافة الحقيقية لسبيكة المنيوم 380 باستخدام السباكة بالعصر

Author: د. فاروق منصور مهدي د. نجيب سلمان عبطان سعد رمضان احمد
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2013 Volume: 20 Issue: 4 Pages: 11-17
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This present study shows ,the effect of applying pressure at rang(10-84) MPa using squeeze casting process to improve the microstructure and actual density of Alumium alloy A380 was studied .From fig(5) its clear that ,the microstructure of prepare casting samples consist of two phases hard eutectic (Al-Si) and Primary α-Al.The effect of applying pressure leads to increase the surface fraction percentage of eutectic phase at (68-84) MPa, but the eutectic percentage was decreased at the same range the actual density was increased at (10,17,84)MP

تم في هذا البحث دراسة تاثير الضغط المسلط ضمن المدى (10-84) ميكاباسكال خلال عملية السباكة بالعصر المباشر على البنية المجهرية والكثافة الحقيقية لسبيكة المنيوم 380 من الخردة , تبين من خلال البنية المجهرية ان البنية تتكون من طورين هما طور اليوتكتك الصلد وطور الالمنيوم الاولي وكذلك وجدنا من خلال علاقة الضغط المسلط وكسر المساحة لطور اليوتكتك ان نسبة كسر المساحة تزداد عند الضغوط (68,84) ميكاباسكال بينما قلت هذه النسبة عند الضغوط (10,17,34) ميكاباسكال . ومن خلال دراسة العلاقة بين الضغط المسلط بمدياته الخمسة والكثافة الحقيقية نلاحظ زيادة الكثافة بزيادة الضغط المسلط (10-17) ميكاباسكال وكذلك عند الضغط (84) ميكاباسكال.

Listing 1 - 8 of 8
Sort by
Narrow your search

Resource type

article (8)


Language

English (6)

Arabic (2)


Year
From To Submit

2015 (2)

2013 (1)

2012 (2)

2011 (2)

2009 (1)