The Effect of Thermal Annealing on the Structural and Optical Properties of CdS Thin Films Deposited by Vacuum Evaporation Method
تأثير المعاملة الحرارية على الخصائص التركيبية والبصرية لأغشيه CdS الرقيقة المحضرة بطريقة التبخير الفراغي

Author: Faris S. Atallah فارس صالح عطالله
Journal: Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة ISSN: ISSN: 19918941 Year: 2013 Volume: 7 Issue: 1 Pages: 129-133
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

: Cadmium Sulphide (CdS) thin films were grown on glass substrates by the vacuum evaporation technique. The effect of thermal annealing on the structural and optical properties of the as deposited samples was analyzed. Structure of these films was characterized by X-ray diffraction . CdS films deposited have polycrystalline structure cubic(zinc blende) and hexagonal (demand) .The grain size increases with increasing annealing temperature. The optical properties of CdS films have highly transmittance in visible region of spectrum and reach to more than 84% . Band gap decreases from 2.55 to 2.33 eV with the increasing annealing temperature from 473K to 623 K..

أغشية رقيقة من مادة كبريتيد الكادميوم( CdS ) رسبت على أرضيات زجاجية بطريقة التبخير الفراغي.وتم دراسة تأثير المعاملة الحرارية على الخصائص البصرية والتركيبية. الخواص التركيبة لهذه الأغشية شخصت باستخدام تقنية حيود الأشعة السينية(XRD) حيت بينت ان غشاء CdS يمتلك تركيبا" بلوريا" مكعبا" (خارصين) وسداسيا"(ماس) ومعدل الحجم الحبيبي يزداد مع زيادة درجة حرارة التلدين. الخصائص البصرية درست باستخدام طيف النفاذية،حيث وجد إن غشاء CdS المرسب يمتلك نفاذية عالية في المنطقة المرئية من الطيف وتصل إلى أكثر من 84% مع فجوة طاقة عريضة تقل من 2.55eV الى2.33eV مع زيادة درجة حرارة المعاملة الحرارية.


Article
Structural and Optical Properties ofCdSxTe1-xThin Films Fabricated by Thermal Evaporation.
الخصائص التركيبية والبصرية لاغشيةCdSxTe1-xالرقيقة المحضرة بطريقة التبخير الحراري تحت الفراغ .

Loading...
Loading...
Abstract

CdSxTe1-x films in the range of ( x=0.9 , 0.8, 0.7 ) about 300 nm thickness have been formed on glass substrates by thermal evaporation . X-ray results showed that the CdTe film was polycrystalline with cubic zinc blend structure and had preferred growth of grains along the (111) crystallographic direction.Also, CdS was polycrystalline with hexagonal wurtzitestructure and had preferred growth of grains along (002) crystallographic direction while CdSxTe1-x films studied the phase change with an inversion point related to the x-value . Transmittance and absorbance spectra of the films were measured as a function of wavelength (300-1100)nm . Then the band gap of the films calculated by using absorption spectrum, where the direct optical energy gap for CdTe is 1.48 eV and for CdS is 2.5 eVwhile the direct optical gap ofCdSxTe1-x films be limited to between CdS and CdTe , and varied non-linearly , showing downward with decrease x-value.Also the refractive index (n) of these films are discussed.

تم تحضير اغشية CdSxTe1-x الرقيقـــــــة عند قيم (x) تساوي (0,9 ، 0,8 ، 0،7) وبسمك (300) نانومتر تقريباً على قواعد زجاجية بطريقة التبخير الحراري تحت الفراغ . اظهرت نتائج حيود الاشعة السينية (XRD) ان غشاء تلوريد الكادميوم (CdTe) متعدد التبلور بتركيب مكعبي (ركائز الخارصين) عند اتجــاه النمو الحبيبي المفضل (111) , كما اظهرت نتائج حيود الاشعـــة السينية ان غشاء كبريتيد الكادميوم (CdS) متعدد التبلور ذو تركيب سداسي عند اتجاه النمو الحبيبي المفضل (002) بينما اظهرت نتائج حيود الاشعــــــــــــة السينية لاغشية CdSxTe1-x تغيراً في الطور بالاعتمــــــاد على تغير قيمـة (x) في المزيج . تم قياس اطياف الامتصاص والنفاذ لجميع الاغشية المحضرة كدالــــــة للطول الموجي (λ) ضمن المدى (300-1100) نانومتر . وقد حسبت فجوة الطاقــــــة البصرية (Eg) عن طريق طيف الامتصاص وكانت قيمة فجوة الطاقة البصرية المباشرة لغشاء تلوريد الكادميوم (1,48) الكترون-فولت ولغشاء كبريتيد الكادميوم (2,5) الكترون-فولت . بينما كانت قيمة فجوة الطاقة البصرية لاغشية CdSxTe1-x محصورة بين قيم فجوة الطاقة لكبريتيد الكادميوم وتلوريد الكادميوم , وتغير قيمها لم يكن خطياً حيث تقل قيمة فجوة الطاقة للمزيج كلما قلت قيمـــــــــة (x) . وتم كذلك دراسة معامل الانكسار (n) للاغشية المحضرة .


Article
Determine the Structural and Optical Properties of ZnO Nanoparticles Prepared by Hydrothermal Method
تحديد الخواص التركيبية والبصرية لجسيمات اوكسيد الزنك النانوية المحضرة باستخدام طريقة Solvothermal

Authors: Dunia K.M.Al-Nasrawy --- Mohammed H.K.AL-Mamoori, --- Ahmed.K.Kodeary
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2015 Volume: 13 Issue: 3 Pages: 236-244
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this work ,zinc oxide nanoparticles(powder) with diameter 12.1 nm was prepared using Solvothermal Method. The structural and optical properties of ZnO nanoparticles was studied by X-ray diffraction, atomic force microscopy AFM, EDS, FTIR, UV-Visible absorption spectroscopy and Flourometer spectrum. X-ray diffraction reveal the formation the purity of prepared phase of ZnO particles with hexagonal wurtzite structure . The energy dispersion scattering ( EDS) examination explains the ZnO nanoparticle is purity. The Atomic Force Microscopy ( AFM) shows the spherical shape of nanoparticles with diameter around 60 nm. The optical absorption spectral study identified the blue shift of the sample in comparison to bulk ZnO in three dimensions . fluorescence spectrum at room temperature confirms the strong UV emission around 397 nm and its indicate that the zinc oxide nanoparticles is a purity and don’t contain on a defects.

في هذا البحث ،جسيمات اوكسيد الزنك (باودر) بقطر 12.1 نانومتر حضرت باستخدام طريقة Solvothermal . الخواص التركيبية والبصرية لجسيمات اوكسيد الزنك النانوية المحضرة درست بواسطة حيود الاشعة السينية X-ray Diffraction ، ومطياف القوة الذرية AFM، EDS،FTIR ،UV-Visible absorption spectrophotometer وجهاز قياس طيف الفلورة Fluorescence Flourometer .حيود الاشعة السينية اظهرت ان جسيمات اوكسيد الزنك النانوية المحضرة تكون نقية و ذات تركيب (wurtzite ) السداسي .فحص (EDS) energy dispersion scattering اظهر ان جسيمات اوكسيد الزنك النانوية هي نقية ايضا وخالية من الشوائب .كذلك قياسAtomic Force Microscopy ( AFM) بين ان جسيمات اوكسيد الزنك النانوية ذات شكل كروي بقطر 60 نانومتر .دراسة طيف الامتصاص البصري للجسيمات النانوية بينت وجود ازاحة زرقاء blue shift بالمقارنة مع اوكسيد الزنك الاساسي في ثلاث ابعاد (bulk zinc oxide (.طيف الفلورة عند درجة حرارة الغرفة اظهر انبعاث قوي عند المنطقة فوق البنفسجية ( ( UV-regionحول 397 نانومتروهذا يشير الى ان جسيمات اوكسيد الزنك النانوية المحضرة هي نقية وغير محتوية على شوائب.


Article
Structural and Optical properties of Polymers(PVA / PVP ) doped with V2O5 composites films

Author: Ghuzlan S. Ahmed
Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: 16094042/25213407 Year: 2017 Volume: 30 Issue: 2 Pages: 16-24
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Study the effect of doping V2O5 on polymers poly vinyl alcohol ( PVA), poly vinyl pyrrolidone (PVP) on the optical and structural properties for film prepared by using Casting method at thickness( 300±20)nm ,All the materials dissolved in distilled water by magnetic mixer for one hour .The optical parameters measured by using UV-VIS spectrometer ,and the structural parameters measured by X-ray diffraction .when measured the energy gap found that the value was decreases from 4.6 eV to 2.98 eV with doping .The refractive index ,extinction coefficient ,absorption coefficient ,real and imaginary dielectric constants of (PVA/PVP) are increasing with doping by V2O5 and with increase the ratio of dop


Article
Structural and optical properties for nano GaxSb1-x films
الخصائص التركيبية والبصرية لأغشية GaxSb1-x النانوية

Authors: A.H.Jalaukhan علي حسين عبدالرزاق --- H.Kh.Al-Lamy حسين خزعل اللامي --- M.F.A.Alias ميسون فيصل أحمد الياس
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2012 Volume: 10 Issue: 18 Pages: 24-28
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Alloys of GaxSb1-x system with different Ga concentration (x=0.4, 0.5, 0.6) have been prepared in evacuated quartz tubes. The structure of the alloys were examined by X-ray diffraction analysis (XRD) and found to be polycrystalline of zincblend structure with strong crystalline orientation (220). Thin films of GaxSb1-x system of about 1.0 μm thickness have been deposited by flash evaporation method on glass substrate at 473K substrate temperature (Ts) and under pressure 10-6 mbar. This study concentrated on the effect of Ga concentration (x) on some physical properties of GaxSb1-x thin films such as structural and optical properties. The structure of prepared films for various values of x was polycrystalline. The X-ray diffraction analysis (XRD) for GaxSb1-x showed that the preferential orientation was (111) for all values of Ga concentration. The grain size was varied with Ga concentration. The optical analysis is performed with the FT-IR spectrophotometer. The optical measurement showed that GaxSb1-x thin films has direct energy gap .It is found that the optical energy gap increased when x increased with the range (x=0.4, 0.5 and 0.6). The optical constant for GaxSb1-x films was varied with increasing x. These prepared polycrystalline GaxSb1-x thin film was a good candidate for use as a base layer material in thermo photovoltaic (TPV).

تم تحضير سبائك GaxSb1-x بتركيز مختلفة من الكاليوم (x=0.4,0.5 and 0.6) في أنابيب الكوارتز المفرغة.تم فحص تركيب السبائك المحضرة بواسطة تحليل حيود الاشعة السينية (XRD) ووجد بأنها متعددة التبلور لتركيب zincblend باتجاهية (220). تم تحضير أغشية GaxSb1-x بسمك واحد ميكرون بطريقة التبخير الوميضي ومرسبة على زجاج بدرجة حرارة اساس 473 كلفن وتحت ضغط 6-10 ملي بار. هذه الدراسة ركزت على تأثير تركيز الكاليوم (x) على بعض الخصائص الفيزيائية لأغشية GaxSb1كالخصائص التركيبية والبصرية.أظهر تحليل الاشعة السينية بان اغشية GaxSb1-x تمتلك اتجاهية(111) لجميع تركيز الكاليوم .يتغير الحجم الحبيبي مع تغير تركيز الكاليوم . تم دراسة الخواص البصرية باستخدام مطياف FT-IR . أثبتت الخصائص البصرية ان أغشية GaxSb1-x تمتلك فجوة طاقة مباشرة. وجد ان فجوة الطاقة البصرية تزداد بزيادة تركيز الكاليوم (0.4,0.5,0.6) .تتغير قيم الثوابت البصرية بزيادة نسبة الكاليوم (x) .جميع الاغشية المحضرة GaxSb1-x المتعددة التبلور تعتبر مرشحا جيدا لاستخدامها كطبقة أساس في الفوتوفولتائية الحرارية (TPV) .


Article
Effect of annealing temperature on the structural and optical properties of ZnS thin films deposited by CBD
تأثير المعاملة الحرارية على الخواص التركيبية والضوئية للأغشية الرقيقة لمركب كبريتيد الخارصين ZnS المحضرة بطريقة ترسيب الحمام الكيميائي.

Author: Mohammad M. Ali* محمـــــــد محســــن علي
Journal: basrah journal of science البصرة للعلوم ISSN: 18140343 Year: 2015 Volume: 33 Issue: 1A Pages: 156-181
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

Zinc sulfide thin films were deposited on glass substrates by using chemical bath deposition (CBD) technique at 90oCand annealed at different temperatures (250, 300 and 350oC) in air for 30 minutes. The chemical bath contains the solutions of thiourea, zinc sulphate, ammonia and hydrazine hydrate. Effect of annealing temperature on the microstructure and optical properties of ZnS thin films were investigated. The structural and optical properties of ZnS thin films were characterized using X-ray diffraction [XRD] and UV-Visible-NIR spectrometry. The XRD analyses indicate that ZnS thin films have zinc blende (cubic) structures with (111) preferential orientation. The structural parameters like lattice parameter, crystallite size, micro strain and dislocation density are calculated. The crystallinity is apparently improved with the increase of annealing temperature. The average grain size was found to be 1.9198 nm and after annealing the grain size was 2.1612 nm, 4.2821 nm and 5.7720 nm respectively (grain size increase with the increase of annealing temperatures, whereas dislocation density and micro strain decreases with the increase of annealing temperatures). It is also found that film surface changes to ZnO after the film is annealed at 300-350oC. The transmittance, absorbance and reflectance are recorded in the range of 300-1000 nm, the optical band gap is direct with a value of 3.85eV, but this value decreased to 3.42eV with annealing temperature at 350oC. The result showed that the CBD ZnS thin films annealed at 350oC exhibit the highest transmittance of about 95.50%. The refractive index(n), extinction coefficient(k), optical conductivity and real and imaginary parts of dielectric constant are evaluated. Additionally, the increase of annealing temperature will increase the pores in films, which results in the decrease of refractive indices and increase of extinction coefficients of the film.

حضرت الاغشية الرقيقة لمركب كبريتيد الخارصين ZnS على القواعد الزجاجية باستخدام تقنية ترسيب الحمام الكيميائي (CBD) بدرجة حرارة ترسيب 90oC للحمام المائي وقد تم معاملة تلك الأغشية الرقيقة حراريا بدرجات حرارية مختلفة (250, 300 and 350oC) في الهواء وبزمن قدره 30 دقيقة. يحتوي الحمام الكيميائي على محاليل الثيوريا وكبريتات الخارصين والامونيا وهيدرات الهيدرازين. تم التحقق من تأثير درجة حرارة المعاملة الحرارية على خواص التراكيب الدقيقة ( المجهرية ) والضوئية للأغشية الرقيقة لمركب ZnS . تم تشخيص الخواص التركيبية والضوئية للأغشية الرقيقة لمركب ZnS بواسطة حيود الاشعة السينية ومطياف الأشعة فوق البنفسجية-والمرئية-والقريبة من تحت الحمراء (UV-VIS-NIR) . تشير تحليلات حيود الاشعة السينية الى ان الأغشية الرقيقة لمركب ZnS تمتلك التركيب البلوري المكعب (zinc blende) وبأتجاه نمو مفضل (111) . تم حساب المعاملات التركيبية مثل معامل الشبيكة والحجم البلوري (الحبيبي) والأجهاد الدقيق وكثافة الأنخلاع. نلاحظ تحسن التبلور مع الزيادة بدرجة حرارة المعاملة الحرارية، وقد كان معدل الحجم الحبيبي قبل المعاملة (1.9198 nm) وبعد المعاملة الحرارية اصبح (2.1612 nm) و (4.2821 nm) و (5.7720 nm) على التوالي ( وذلك يدل على ان الحجم الحبيبي يزداد بزيادة درجة حرارة التلدين، بينما يقل الاجهاد الدقيق وكثافة الانخلاع مع زيادة درجة حرارة التلدين ). كذلك وجدنا تغير سطح الغشاء لمركب ZnS الى ZnO بعد معاملة الأغشية بدرجة حرارة ما بين 300-350oC . تم تسجيل النفاذية والامتصاصية والانعكاسية لأغشية ZnS بمدى الاطوال الموجية 300-1000 nm ، تم حساب فجوة الطاقة للانتقال المباشر وكانت قيمتها 3.85eV ولوحظ نقصان فجوة الطاقة الى 3.42eV مع التلدين. نلاحظ من دراسة النفاذية ان الأغشية الملدنة بدرجة حرارة 350oC تمتلك أعلى نفاذية بحدود 95.50% . تم حساب معامل الانكسار ومعامل الخمود وكذلك الجزء الحقيقي والجزء الخيالي للثوابت البصرية والتوصيلية الضوئية. أن زيادة درجة حرارة التلدين تعمل على زيادة المسامات في الأغشية، والتي ينتج عنها نقصان في معامل الانكسار وزيادة في معامل الخمود للغشاء.


Article
Effects of Gamma Radiation on Optical and Structural Properties of Cadmium Telluride Thin Films
تأثير اشعة جاما(γ) على الخواص التركيبة والبصرية لأغشية الكادميوم تيلورايد (CdTe)

Authors: Hayder Mohammad Ajeel --- Zainab T. Hussein --- Khalid M.Thajeel --- Rassol Hussein Mekkilf
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 4 Part (B) Scientific Pages: 811-818
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Cadmium Telluride (CdTe) thin films were prepared by thermal evaporation technique in the vacuum of about 3 × 10−3 mbar .using commercial glass substrates. The CdTe thin films were the effect gamma (γ) radiation on the grain size with dose 0.5µCi and membrane surface of treated films before and after to exposure period to gamma radiation and characterized by X-ray diffraction (XRD) results showed that the films are polycrystalline structure with hexagonal lattices and had preferred growth of grains along the (002) crystallographic direction. Atomic Force microscopy (AFM) and optical microscopic recognized. The optical band gap of thin films was found to allow direct transition with energy gap of 1.7 eV.

حُضًرت أغشية الكادميوم تيلورايد بتقنية التبخير الحراري في الفراغ 3 × 10−3 ملي بار. باستخدام قواعد زجاجية. تم دراسة تأثير اشعة جاما )γ( بجرعة 0.5µCiعلى الحجم الحبيبي وعلى سطح الغشاء قبل وبعد التعرض لأشعة غاما )γ( لفترات زمنية مختلفة وخصائص الاغشية المحضرة باستخدام حيود الأشعة السينية (XRD)، ، فحص المجهري البصرية ((UV-VIS ومجهر القوة الذرية (AFM) , حيث أظهرت النتائج حيود الأشعة السينية أن الأغشية كانت متبلورة كما أظهرت أن الاغشية كانت ذات تركيب سداسي، وافضل نمو الحبوب على طول الاتجاه (002) للبلورات. وأظهرت صورمجهر القوة ذرية (AFM) المجهر الضوئي له. وجد ان فجوة الطاقة للأغشية الكادميوم تيلورايد للانتقال المباشرة (1. 7 ) الكترون فولت.


Article
A Study on Structural and Optical Properties of Nanostructure MgxZn1-xO Thin Films Using Pulsed Laser Deposition
دراسة الخصائص التركيبية والبصرية للاغشية الرقيقة ZnO المشوبة ب Mg ذات التراكيب النانوية باستخدام تقنية الليزر النبضي

Authors: Ali A. Yousif --- Marwa A. Abd-Majeed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 6 Part (B) Scientific Pages: 1030-1050
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

For this paper, films have been grown under various deposition conditions in order to understand the effect of processing on the film properties and to specify the optimum condition, namely substrate at temperatures of 400°C, oxygen pressure (2×10-1) mbar, laser fluence 400 mJ, and with different Mg doping (x=0, 0.02, 0.04, 0.06), using double frequency Q-switching Nd:YAG laser beam (wavelength 532nm), repetition rate (1-6) Hz and the pulse duration of (10 ns), to deposit MgxZn1-xO films on glass substrates with thickness of about 200±10 nm for all MgxZn1-xO films at different deposition condition and the number of laser pulses was 100 pulses. The X-rays spectra revealed that the presence of diffraction peaks indicates that the polycrystalline of the films depended strongly on the Mg-content in the layers. All the grown films is (101) as predominant reflection. The Scanning Electron Microscopy (SEM) images, the average grain size less than 50 nm. From the study of atomic force microscopy (AFM), we can determine the root mean square (RMS) surface roughness of Mg doped ZnO films. The optical properties were characterized by the transmittance and absorption spectroscopy at room temperature, measured in the range from (300 - 900) nm. For all the films, the average transmittance in the visible wavelength region λ = (400 - 800) nm is greater than (70%). The maximum value of the transmittance is greater than (95%) was obtained for these films. (Eg) values of MgxZn1-xO thin films are (3.37, 3.59, 3.82, and 4)eV corresponding to the Mg-content (x = 0, 0.02, 0.04 and 0.06) respectively. In other word, the optical band gap of MgxZn1-xO thin films become wider as Mg-content increases and can be precisely controlled between 3.37 and 4eV.

تم في هذا البحث دراسة نمو الاغشية بظروف ترسيب مختلفة لفهم تاثير طريقة التحضير على خصائص الغشاء و لتحديد افضل الظروف التحضيرية وتتمثل بدرجة الحرارة ,400°C وضغط الاوكسجين(2×10-1) mbar , كثافة طاقة الليزر الساقطة 400mJ وباختلاف تشويب المغنيسيوم (x=0, 0.02, 0.04, 0.06) باستخدام التردد المضاعف لليزر النيديميوم- ياك والذي يعمل بتقنية عامل النوعية عند الطول الموجي 532nm بمعدل تكرارية (1 – 6) هرتز وامد نبضة 10 نانوثانية لترسيب اغشية اوكسيد الخارصين المشوب بلمغنيسيوم MgxZn1-xO على قواعد من الزجاج بسمك 200±10نانومتر وعدد نبضات 100 نبضة لكل الاغشية باختلاف ظروف الترسيب. أطياف الأشعة السينية اثبتت بأن نتائج قمم الحيود تشيرالى ان درجة التبلور للاغشية تعتمد بقوة على كمية المغنيسيوم في الطبقات. جميع الأغشية المنماة تمتلك المستوي (101) كانعكاس سائد هي أغشية ذات تركيب سداسي متعددة التبلور يكون فيها المستوي (101) هو المستوي السائد. قياسات المجهر الالكتروني الماسح فقد وجد ان معدل الحجم الحبيبي كان اقل من50 نانومتر . من دراسة مجهر القوى الذرّيه نسطيع أن نحدد مربع الجذر المتوسط (RMS) لخشونة سطح اغشية اوكسيد الخارصين المشوبة بالمغنيسيوم. الخصائص البصرية تمت دراستها بوساطة قياس طيف النفاذية والامتصاصية عند درجة حرارة الغرفة, لمدى طول موجي يتراوح من (300 - 900) nm . معدل النفاذية لجميع الأغشية للمنطقة المرئية من الطيف λ = (400 - 800) nm تكون اكبر من ( 70 % ) وتصل في احدى النماذج لاكثر من ( 95 %) . ان قيم فجوة الطاقة ( (Egلهذه الأغشية تساوي ( 3.37, 3.59, 3.82, 4) الكترون- فولت لكل من التراكيز ( x = 0, 0.02, 0.04, 0.06) على التوالي. كما ان قيم فجوة الطاقة تزداد بزيادة نسبة المغنيسيوم في الأغشية ويمكن التحكم بقيمة فجوة الطاقة بالضبط بين (3.37 و (4 الكترون – فولت.


Article
Structural and optical properties of different thicknesses nano-crystalline Pb0.2Cd0.8S prepared by chemical bath deposition

Authors: Raad S. Sabray --- Wisam J. Aziz --- L. A. Latif --- Huda J. Ali
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2015 Issue: 3 Pages: 159-170
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this study, nanostructure thick films of Pb0.2Cd0.8S were prepared by the chemical bath deposition technique on glass slides at 343 K with different thicknesses ( 2.65 , 3 and 3.58)μm.The surface morphology of films which characterized by AFM and SEM revealed the formation started in low thickness with small islands to reach the final structure formation in 3.58μm with nano sheets (Like- stars) and homogenous for whole area of top surface and the spherical crystallite size of the films is found to range from 50 nm to 100 nm. The optical absorption and transmission properties of films were determined by UV spectrophotometry.The energy band gap values were increased with thickness increased as 2.65 μm (2eV), 3 μm (2.2 eV) and 3.85 μm (2.23 eV) according to the principle of thickness relation with energy band gap.


Article
Effect of Annealing Temperature on Structural and Optical Properties of CdS Thin Films

Authors: Alaa S. Al-Kabbi --- Saeed J. Abbas --- Mohammad M. Ali
Journal: Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) ISSN: 18172695 Year: 2019 Volume: 45 Issue: 1A Pages: 1-13
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

The CdS thin films were deposited on glass substrates by two different methods, chemical bath deposition (CBD) and thermal evaporation (T.E.). The effect of annealing temperature on the structural and optical properties of the CdS thin films were investigated. The structural properties of CdS thin film was studied by X-ray diffraction. It was observed that the films have a polycrystalline hexagonal (wurtzite) structure with preferred orientation along (002) plane. The crystallite size calculated from XRD increases as the annealing temperature is increased. We observed that the lattice constant, micro strain, dislocation densities and number of crystallites per unit area of the films are quite different in these processes from XRD analysis by considering high intense diffraction peaks of the as-deposited and annealed films. The energy band gap in nanocrystalline CdS thin films has been estimated from absorption measurements. The band gap values for CBD-CdS thin films decreased from 2.75 to 2.45 eV and for T.E.-CdS thin films decreased from 2.60 to 2.43 eV with increasing annealing temperature. Small nanocrystals display wide band gaps as a result of the quantum confinement experienced by nanocrystals of a certain size

Listing 1 - 10 of 21 << page
of 3
>>
Sort by
Narrow your search

Resource type

article (21)


Language

English (16)

Arabic (4)

Arabic and English (1)


Year
From To Submit

2019 (1)

2018 (2)

2017 (2)

2016 (3)

2015 (3)

More...