Fabrication of carbon nanopowder by arc discharge technique
تصنيع مسحوق الكاربون النانوي باستخدام تقنية التفريغ الكهربائي القوسي

Loading...
Loading...
Abstract

Carbon Nanopowder was fabricated by arc discharge technique at deposition pressure of 10-5 mbar Argon gas on glass substrates. The prepared carbon nano- powder was collected from chamber and purified with nitric acid at 323K .The morphology and crystalline structure of the prepared powder was examined by X-Ray Diffraction (XRD), Atomic Force Microscope (AFM), and Scanning Electron Microscope (SEM). XRD spectrums showed that the powder exhibits amorphous structure and after purification, the powder showed hexagonal structure with a preferential orientation along(002) direction ,where AFM and SEM gave very compatible estimation on the grain size and shape of the nanopowder.

تم تصنيع مسحوق الكربون النانوي باستخدام تقنية التفريغ ألقوسي( تحت ضغط بحدود10-5 ملي بار غاز الاركون )على شرائح زجاجية ،جمع المسحوق من الحاضنة وتنقيته باستخدام حامض النتريك عند درجة حرارة 323 كلفن .تم فحص التركيب البلوري وسطح العينات خلال حيود الأشعة السينية (XRD) ومجهر القوة الذرية (AFM) ومجهر الماسح الالكتروني (SEM) .أظهرت نتائج الأشعة السينية تركيبا عشوائيا للمسحوق الغير معامل ومتعدد التبلور للمسحوق المعامل مع تركيب سداسي مفضل باتجاه (002) .كما ان فحوصات (AFM)، (SEM) اظهرت توافقا مع الحجم الحبيبي المحسوب وشكل المسحوق النانوي المصنع.


Article
NANO AND MICRO INDIUM OXIDE STRUCTURE PREPARED USING LASER ABLATION METHOD

Author: Makram A.Fakhri* Sarmad Fawzi Hamza*
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2013 Volume: 13 Issue: 1 Pages: 120-128
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In the present work, effect of laser energy on optical and morphological properties of In2O3 trioxide thin film has been carried out using Reactive Pulsed Laser as a Deposition technique (RPLD). Q-switch Nd-YAG laser with (λ=1.06nm,tb=7nsec) and different energy's has been use to ablated pure indium target and deposited on glass substrates and constant substrate temperature of (333K). The results films show that high transparency reached to about (80-95) % can be achieved with In2O3 film which itself decreases sharply with the decreasing of laser energy while the optical band gap is( 3.6-3.8) eV at optimum laser energy (400mj ). The optical properties of the prepared include optical microscopic measurement, optical transition measurement, surface uniformity measurement and FTIR.

في هذا العمل قد تم تنفيذ تأثير لطاقة الليزر على الخصائص البصرية والتركيبة للأغشية الرقيقة لثالث اوكسيد الانديوم In2O3 بأستخدام تقنية الترسيب بالليزر النبضي الفعال (RPLD) .Q -switch ND- YAG الليزر مع ( (λ =1.06nm وامد نبضة ( 7nsec) حيث يعمل الليزر على ترسيب ذرات اوكسيد الانديوم المتبخرة بتأثير الليزر على قواعد من الزجاج . ودرجة الحرارة الفاعدة (333K). تظهر النتائج التي تم تحقيقها شفافية عالية وصلت الى %(80-95) مع In2O3 حول الغشاء الذي يقل بشكل حاد مع انخفاض طاقة الليزر وكذلك تم الحصول على فجوة طاقة البصرية eV ) 3.6 – 3.9 ) في طاقة الليزر الامثل (400mj) . الخصائص البصرية للمعدة وتشمل قياس المجهرية الضوئية , والنفاذية , والانعكاسية , وقياسا بالمجهر القوة الذرية وتحويلات فورير لمطيافية المنطقة تحت الحمراء .


Article
Effect of Substrate Temperature on Optical and Structural Properties of Indium Oxide Thin Films Prepared by Reactive PLD Method
تأثير درجة حرارة القاعدة على الخصائص البصرية والتركيبية لاغشية اوكسيد الانديوم الرقيقة المحضرة بواسطة الترسيب بالليزر النبضي

Author: Makram A. Fakhri
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 5 Part (A) Engineering Pages: 1323-1330
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present Work, effect of substrate temperatures on the optical and morphological properties of In2O3 trioxide thin film has been carried out using Reactive Pulsed Laser as a Deposition technique (RPLD). 1.064µm, 7 nsec Q-switch Nd-YAG laser with 400 mJ/cm2 laser energy’s has been used to ablated pure Indium target and deposited on glass substrates . The resulted films show High transparency reached to about (85) % which found to decrease sharply with the substrate temperatures. The estimated optical band gap found to be about 3.6eV at optimum substrate temperatures (70 Co). The FTIR results insure the formation ofIn-O vibrational bond with different vibrational intensity depending on substrate temperatures.

تم في هذا البحث دراسة تاثير درجة حرارة القاعده على الخصائص البصريه والمورفولوجيه لسطح الاغشية الرقيقة المحضرة بطريقة الترسيب بالليزر النبضي . تم استخدام ليزر نديميوم ياك النبضي يعمل بضابط عامل نوعيه بطول موجي 1.06 مايكرومتر و امد نبضة 7 نانوثانيه وبطاقة 400 ملي جول/سم2 لغرض اجراء عملية الاستئصال لسطح معدن الندميوم عالي النقاوه ولغرض الترسيب على سطح القواعد الزجاجيه. اظهرت نتائج الخصائص البصريه النفاذية العالية للاغشية المحضرة والتي تصل ال 85% والتي سرعان ما تهبط بشدة مع نقصان درجة حرارة القاعدة . القيمة المحسوبه لفجوة الطاقة وجدت لتكون حوالي 3.6الكترون فولت عند الدرجة الحرارية التي اختيرت لتكون المثلى ((70Co. نتائح النفاذية للمنطقة تحت الحمراء FTIR اكدت وجود الاصرة نوع الاهتزازي بين مادتي الانديوم – الاوكسجين وبشدات اهتزاز مختلفه بالاعتماد على درجة الحرارة.


Article
Effect of Experimental Parameters on the Fabrication of Silver Nanoparticles by Laser Ablation
تأثير العوامل التجريبية على تشكيل فضه نانوية بعمليه القلع المستحث بأشعة الليزر

Authors: Mohammed J. Haider --- Mohammed S. Mehdi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 4 Part (B) Scientific Pages: 704-709
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, silver nanoparticles has been prepared via ablation of pure Ag metal target in distilled water was accomplished using Q-switched Nd:YAG laser at (1.06 µm) laser wavelength , with different laser energy and number of laser pulses. The effect of these parameters on the optical and surface morphology have been studied , UV-Visible show a red shift in the absorption spectra related to the shift in the energy gap due to increment of the grain of prepared particles size is increased as laser energy. Grain size of the obtained NPs are found to increase with laser energy with rang (20-112) nm as shown by the SEM result.

في هذا العمل تم أجراء عملية التبخير بالليزر لشريحة معدنية من الفضة النقي مغمورة بماء مقطر لا أيوني وباستخدام ليزر الندميوم-ياك النبضي بالطولي الموجي 1.06 µm)) وكثافة طاقات ليزر مختلفة وبعدد نبضات مختلف. تم دراسة تأثير هذه المعلمات المختلفة على الخصائص البصرية، خصائص طبوغرافية السطح أظهرت نتائج الخصائص البصرية حدوث إزاحة نحو الأطول الموجية الحمراء في طيف الامتصاص للمحاليل المحضرة وذلك نتيجة لإزاحة فجوة الطاقة بسبب زيادة الحجم الحبيبي للدقائق المحضرة مع زيادة طاقة الليزر، بينما لوحظ وجود إزاحة نحو اللون الأزرق مع الزيادة في عدد النبضات. وكذلك وجد أن الحجم الحبيبي للجسيمات النانوية بأنها تزداد مع زيادة طاقة الليزر وبمعدل من 20-112 نانوميتر.


Article
Rapid thermal oxidation of copper nanostructure thin film for solar cell fabrication
الأكسدة الحرارية السريعة للتراكيب النانوية لاغشية اوكسيد النحاس في تصنيع الخلايا الشمسية

Author: Makram A. Fakhri مكرم عبد الطلب فخري
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2015 Volume: 13 Issue: 27 Pages: 70-75
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In the present work is the deposition of copper oxide using the pulsed laser deposition technique using Reactive Pulsed Laser as a Deposition technique (RPLD), 1.064μm, 7 nsec Q-switch Nd-YAG laser with 400 mJ/cm2 laser energy’s has been used to ablated high purity cupper target and deposited on the porous silicon substrates recorded and study the effect of rapid thermal annealing on the structural characteristics, morphological, electrical characteristics and properties of the solar cell. Results of AFM likelihood of improved absorption, thereby reducing the reflection compared with crystalline silicon surface. The results showed the characteristics of the solar cell and a clear improvement in the efficiency of the solar cell in the case of copper deposition or not.

في العمل الحالي تم ترسيب أكسيد النحاس باستخدام تقنية الترسيب بالليزرالنبضي، حيث تم استخدام لیزرندیمیومیاك النبضي یعمل بضابط عامل نوعیة بطولموجي 1.06 مایكرومتر وامد نبضة 7 نانوثانیة وبطاقة 400 مليجول/سم 2لغرض اجراء عملیة الاستئصال لسطح معدن النحاس عالي النقاوة والترسیب على سطح القواعد السليكون المسامي. حيث تم دراسة تأثير التلدين الحراري السريع على الخصائص التركيبية والسطحية والخصائص الكهربائية وخصائص الخلية الشمسية. اظهرت نتائج AFM احتمال تحسين الامتصاص، مما يقلل من الانعكاس مقارنة مع سطح السيليكون البلورية و أظهرت النتائج تحسنواضح بخصائص الخلايا الشمسية (الكفاءة) في حالة ترسيب اوكسيد النحاس من عدمه.


Article
Effect of Electrodes Separation in DC Plasma Sputtering on Morphology of Silver Coated Samples

Authors: Khalid A. Yahya --- Ban F. Rasheed
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2016 Volume: 19 Issue: 4 Pages: 78-85
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this work, the effect of the electrodes separation on plasma parameters and morphology properties for coated glass samples by silver metal using low voltage DC discharge plasma sputtering source. At fixed argon gas pressure 0.2 mbar and discharge currents Id(20,30,40,50 and 60)mA, for different electrodes separation d (3,4,4.5,5,6)cm was studied. The plasma sputtering source consists of a cylindrical chamber including two circular electrodes made from stainless steel. The cathode electrode is carrying the silver metal as a target and permanent magnet, while a glass sample coater is placed on the anode electrode. The plasma parameters: temperature of electron(Te) and ion density(ni) were determined by using cylindrical single Langmuir probe. Also, the surface morphology for the coater samples were studied by atomic force microscope (AFM). The results of this work shown that a linear increases in ions density and an exponential decreasing in electron temperature for different electrodes separation. Furthermore, the relationship between the average grain diameter and average grain height as a function of electrodes separation are nonlinear. The minimum average grain diameter is (90 nm) at d=4 cm for Id=40 mA and minimum average grain height is (5.5 nm) at the same electrodes separation and discharge current. When the temperature of electron increased, the values of average grain diameter increased while the values of average grain height decreased.

تم في هذا العمل, د ا رسة تأثير المسافة بين القطبين علىمعلمات البلازما وخصائص اشكال سطح النموذج المطليبالفضة باستعمال مصدر للترذيذ البلازمي للتفريغ عندالفولتيات الواطئة المستمرة في الترذيذ البلازمي بضغط غازالاركون الثابت ) 0.2 ( ملي بار لتيا ا رت التفريغ( 20,30,40,50,60 ( ملي امبير لعدة مسافات بين القطبين( 3,4,4.5,5,6 ( سم.يتكون مصدر الترذيذ البلازمي من حجرة اسطوانية تحتويعلى قطبين دائرين مصنوعين من مادة الستنلس ستيل. قطبالكاثود يحمل مادة الهدف والمغناطيس الثابت بينما يوضعالنموذج الزجاجي لطلائه على قطب الانود.عوامل البلازما, درجة ح ا ررة الالكترون وكثافة الايونات تمتحديد باستعمال مجس لانكمور الاسطواني المنفرد وايضادرست خصائص اشكال سطوح النماذج المطلية بواسطةمجهر القوة الذرية.أوضحت نتائج هذا البحث زيادة خطية في كثافة الايوناتونقصان بدالة أسية في درجة ح ا ررة الالكترون بزيادة المسافةبين القطبين. كما ان العلاقة بين معدل قطر الحبيبةوارتفاعها كدالة غير خطية للمسافة بين القطبين. اقل معدلقطر الحبيبة وارتفاعها هو ) 90 ( نانومتر عند المسافة (4) سموبتيار تفريغ ) 40 ( ملي امبير, واقل معدل ارتفاع الحبيبة هو( (5.5 نانومتر بنفس المسافة بين القطبين وتيار التفريغ.عند زيادة درجة ح ا ررة الالكترون فان قيم معدل قطرالحبيبة يزداد ويقل ارتفاعها.


Article
Analysis the Surface Morphology of the Porous Media by using Atomic Force Microscope technique
أستقصاء مورفولوجيا السطوح المسامية بوساطة استخدام مجهر القوة الذري

Author: Bashir Y. Sherhan Al-Zaidi بشير يوسف شرهان
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2017 Volume: 13 Issue: 4 Pages: 98-110
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

An atomic force microscope (AFM) technique is utilized to investigate the polystyrene (PS) impact upon the morphological properties of the outer as well as inner surface of poly vinyl chloride (PVC) porous fibers. Noticeable a new shape of the nodules at the outer and inner surfaces, namely "Crater nodules", has been observed. The fibers surface images have seen to be regular nodular texture at the skin of the inner and outer surfaces at low PS content. At PS content of 6 wt.%, the nodules structure was varied from Crater shape to stripe. While with increasing of PS content, the pore density reduces as a result of increasing the size of the pore at the fiber surface. Moreover, the test of 3D-AFM images shows that the roughness of both surfaces of fibers seems to be decreased with PS content. Alternatively, the fibers pure water permeability (PWP) has been declined with decreasing of fiber roughness.

يتعلق البحث بدراسة سطوح المواد المسامية وفحصها والتي تحتوي فتحات على سطحها تقود الى شبكة ذات ابعاد احادية او ثنائية او ثلاثية في داخل البناء الهيكلي لها وذلك باستخدام تقنية مجهر القوى الذري (AFM-technique). ان هذه التقنية تم استخدامها في البحث لدراسة تاثير محتوى البولي ستايرين على خواص السطوح الخارجية والداخلية لالياف البولي فنيل كلورايد المسامية عن طريق تغير مورفولوجيا السطح المسامي. وتم ملاحظة شكلاً لعقد مميز على السطوح الخارجية والداخلية عرفت علميا باسم: "Crater nodules". حيث ان صور الالياف المستنبطة من خلال مجهر القوة الذري اوضحت ان تركيب العقد على السطوح الداخلية والخارجية كان منتظما عند استخدام محتوى قليل من البولي ستايرين. وعند تركيز 6% من مادة البولي ستايرين تم ملاحظة تغير الشكل الهيكلي للعقد من "Crater" الى ."Stripe" ان زيادة محتوى البولي ستايرين ادى ايضا الى نقصان كثافة المسامات مع زيادة حجمهاعلى سطوح الالياف. الصور ثلاثية الابعاد لمجهر القوى الذري دلت كذلك على ان زيادة محتوى البولي ستايرين ادى الى نقصان خشونة السطوح الداخلية والخارجية لذلك فمعدل نفاذية الماء عبر الالياف قل مع نقصان خشونة السطوح.


Article
Structural, Surface Morphology and Optical Properties of Bi2O3 Thin Film Prepared By Reactive Pulse Laser Deposition.
الخصائص التركيبية وطبيعة السطح والبصرية لاغشية اوكسيد البزموث الرقيقة المحضرة بواسطة الاقتلاع الفعال لليزر النبضي

Loading...
Loading...
Abstract

In the present work, bismuth oxide Nanostructure thin film was prepared using reactive pulse laser deposition method. Optical, structural and surface morphology properties was carried out and the result insure the formation of polycrystalline Bi2O3 thin film with energy gap of (2.5) eV .The Atomic Force Microscopic Image show a Nano crystalline structure with average grain size of about (75.42 nm) .

في هذا البحث تم تحضير اغشة رقيقة من اغشية البزموث اوكسايد باستخدام طريقة الاقتلاع باليزر النبضي الفعالة . حيث تم دراسة الخصائص البصرية والتركيبية وطبيعة السطح لهذه الاغشية .لقد اكدت النتائج تكون غشاء اوكسيد البزموث متعدد التبلور بفجوة طاقة مقدارها 2.5 اليكترون فولت .اما نتائج مجهر القوة الذرية اظهرت تكون تراكيب بلورية نانوية بحجم حبيبي مقداره 75.45 نانو متر


Article
Preparation and Characterization of (Tio2-Sno2) Thin Films by Pulsed Laser Deposition
تحضير ودراسة اغشية رقيقة مكونة من خليط اوكسيد التيتانيوم واوكسيد القصديربطريقة الترسيب بالليزر النبضي

Authors: Saja H.Rashed --- Adawiya J. Haider --- Samar Younis
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 4 Part (B) Scientific Pages: 658-665
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, mixed oxide (TiO2-SnO2) thin films were grown on Si (111) and glass substrates by pulsed laser deposition (PLD) method. The influences of increasing amounts of SnO2 were investigated. The X-ray diffraction results show the peaks position of the plane was shifted towards higher angle values with increasing amounts of SnO2. The surface morphology of the deposits materials was also studied by using a scanning electron microscope(SEM) The results show that, the grain sizes decreases with increasing SnO2 content from the largest value (53.6)nm to smallest value (25.5) nm. From UV-visible spectroscopy, the distinct variations in the transmission spectra, and optical energy gap, of the thin films were also observed.

يتضمن هذا العمل ترسيب اغشية رقيقة من خليط اوكسيد التيتانيوم واوكسيد القصديرعلى السيلكون والزجاج باستخدام طريقة الترسيب بالليزر النبضي وقد تم مناقشة تاثير زيادة نسبة اوكسيد القصديرعلى خصائص خليط اوكسيد التيتانيوم والقصدير.وقد بينت نتائج حيود الاشعة السينية ان موقع القمم انحرفت باتجاه قيم الزوايا الاعلى بزيادة نسبة اوكسيد القصدير.اما مورفولوجية السطح للمادة المترسبة فقد تم دراستها بواسطة المجهر الماسح الالكتروني .وقد بينت النتائج ان الحجم الحبيبي للجسيمات النانوية قل بزيادة نسبة اوكسيد القصديرمن الحجم الحبيبي( 53.6 نانومتر) الى الحجم الحبيبي (25.5 نانومتر). وكذلك قد تم ملاحظة التغيرات الحاصلة لطيف النفاذية وكذللك فجوة الطاقةالبصرية بواسطة قياسات مطياف النفاذية للأشعة المرئية وفوق البنفسجية.


Article
Synthesis of Nano-TiO2 Thin Films by Sol-gel Dip-coating Method
تصنيع أغشية رقيقة نانوية من ثنائي اوكسيد التيتانيوم باستخدام طريقة محلول-هلام بطريقة الطلاء بالتغطيس

Authors: Bushra R. Mahdi --- Abass F. Al.mamori --- Adnan meship Mahdi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 7 Part (B) Scientific Pages: 1303-1312
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Synthesis of titanium dioxide (TiO2) Thin film on three microscope glasses using sol-gel method has been studied intensively. The starting materials were titanium(III)chloride, Ammonium Hydroxide. The components were mixed together to form the sol. Then, at 50℃ heating and ageing was applied to form stable sol-gel . Every glass substrate dipping in sol-gel beaker for period time (1,3,5)min respectively, for obtaining different thickness films. To evaluate the performance of films, After annealing at 500℃ , the crystallinity of the films was determined by using the x-ray diffractometer (XRD). The change on the surface morphology was observed using Atomic Force Microscope(AFM). Finally, Optical properties measurements Absorbance (A) and transmittance(T)) for (TiO2) films were studied by UV-Visible spectrometer. analysis on the films. It has been successfully shown that the anatase crystalline phase was observed when the TiO2 thin film was annealing at 500°C. The roughness and the crystalline size of TiO2 thin film changed with the thickness. The minimum grain size( 6.92) nm for thickness 1.2µm UV-visible studying that absorption is maximum at UV spectrum (opaque) and the transmittance is maximum at the visible spectrum

تم تحضير اغشية رقيقة من مادة ثنائي اوكسيد التيتانيوم باستخدام تقنية محلول هلامي بطريقة الطلاء بالتغطيس رسبت طبقة رقيقة على شرائح مجهر زجاجية باستخدام تقنية سول- جل المكثف. استخدمت المواد الاولية لتحضير سول- جل من ثلاثي كلوريدالتيتانيوم وهيدروكسيد الامونيوم . خلطت المكونات لتشكيل السول ويتم الخلط بدرجة حرارة 50 درجة مئوية لتشكيل سول-جل.غطست ثلاثة شرائح زجاجية لفترة متفاوتة من (1-3-5) دقيقة في مادة المحضرة للحصول على اغشية بأسماك مختلفة. تم تقييم أداء الافلام المحضرة بعد التلدين بدرجة 500 درجة مئوية . تم تحديد التبلور باستخدام جهاز حيود الاشعة السينية ولوحظ التغير في ميرفولوجية السطح باستخدام مجهز القدرة الذرية. اخيراً درست الخصائص البصرية من امتصاص ونفاذية للغشاء المحضر باستخدام مطياف الاشعة فوق البنفسجية –المرئية. ومن تحليل الاغشية اظهرت نجاح تبلور طور antatag عن تلدين بدرجة 500 درجة مئوية خشونة السطح والحجم الحبيبي لغشاء ثاني اوكسيد التيتانيوم تغير مع تغير السمك. أقل حجم حبيبي 6.92 نانومتر لسمك 1.2 مايكروميتر. وأعظم امتصاص عند منطقة الفوق البنفسجية وأعظم نفاذية في المنطقة المرئية.

Listing 1 - 10 of 11 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (11)


Language

English (10)

Arabic and English (1)


Year
From To Submit

2019 (1)

2017 (1)

2016 (1)

2015 (2)

2014 (3)

More...