Article
Nano Crystalline Titania Powders as Enhancement for 2-(2-Nitrobenzylidene) Hydrazinecarbothioamide as Corrosion Inhibitor

Author: Zeyad Fadhil
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2017 Volume: 20 Issue: 3 Pages: 1-5
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

The present investigation, represent arranging of nano-sized TiO2 powder by method for sol-gel strategy through precursor hydrolysis of Titanium isopropoxide. Morphological reviews gained from SEM micrograph showed the particles with the round shapes are Anatase in nature. Crystalline size of TiO2 powder has procured is 50-75 nm for Anatase at 550 ºC by controlling the sharpness. Weight lessening system has been used to consider the disintegration prevention effectiveness of 2-(2-nitrobenzylidene) hydrazinecarbothioamide enhanced by TiO2 in HCl course of action. The results show that 2-(2-nitrobenzylidene) hydrazinecarbothioamide with TiO2 raise the disintegration productivity from 87 to 96%. Disintegration obstacle viability increases with growing concentration of inhibitor and it moreover augments with extending joining of TiO2

Keywords

TiO2 --- titania --- Surface --- Erosion.


Article
PREPARATION AND CHARACTERIZATION OF PHASE-PURE ANATASE NANOPARTICLES

Author: Dr Imad Ali Disher Al-Hydary
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2014 Volume: 14 Issue: 1 Pages: 98-106
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The anatase phase of titania has great potential to be used in various applications. Thus; the synthesis of phase-pure nanocrystalline anatase has attained great importance in the past decade. In the present work, the sol-gel method was used to prepare such nanoparticles. It has been found that the sol-gel method can, with the help of long aging time, produce phase-pure anatase nanoparticles that have polygonal shape with edges’ length in the range of (~30-70nm). The firing temperature should be kept higher than 500°C to get fully crystalline nanoparticles and lower than 800°C to avoid the phase transformation to rutile phase

يمتلك طور الاناتيس لثنائي اوكسيد التيتانيوم الاهلية للاستخدامات العديدة في التطبيقات المختلفة، لذلك اكتسب تحضيره بشكل متبلور نانوي نقي-الطور اهمية كبيرة في العقد المنصرم. في العمل الحالي استعملت طريقة (المحلول-الجلاتين) في تحضير هذه المادة بالوصف المذكور. لقد وجد ان طريقة (المحلول-الجلاتين) يمكن ان تنتج هذه المادة بمساعدة التعتيق لفترة زمنية طويلة. تمتلك الحبيبات النانوية المحضرة شكلا متعدد الاظلاع تتراوح ابعاد اضلاعه بين (~30 – 70 نانومتر). يجب ان تتم عملية حرق الجلاتين في درجة حرارة اعلى من (500°م) للحصول على الحبيبات النانوية المتبلورة وبدرجة اقل من (800°م) لتفادي تكون طور الروتايل.


Article
Titania Effect on Sintering behavior of Alumina
التأثير التيتاني على سلوكية تلبيد الألومينا

Author: Qasid Abdul Sattar Saleh قاصد عبد الستار صالح
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2009 Volume: 6 Issue: 4 Pages: 770-774
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The sintering behavior of Alumina was investigated by adding TiO2. The addition of TiO2 lowered the sintering temperature of the Alumina compared with those of pure Alumina. The result suggests that TiO2 acts as an activator for sintering of Alumina. Water absorption, apparent porosity and density were examined for both pure and TiO2 added to Alumina samples. The variations of sintering behavior were discussed in terms of shrinkage, porosity, water absorption and density. Thermal shock resistance was also examined. In term of this work, the way of improving the thermal shock resistance in oxide- based materials by adding reactive Titania powder to the Alumina samples. The laboratory results showed an improvement in thermal shock resistance property of the products which open the horizon of development of the final products.

لقد تم التحقق من التأثير التيتاني على عملية التلبيد لنماذج الالومينا من خلال اضافة نسب (2,5,10,15,20) % من التيتانيا الى نماذج الالومينا. وقد دلت النتائج لهذه النماذج بعد مقارنتها مع نماذج الالومينا قبل الاضافة على ان التيتانيا تعمل كعامل مساعد يساعد على تقليل درجة التلبيد لنماذج الالومينا وفي نفس الوقت تحسن في الاداء الحراري لها من خلال تحسين مقاومتها للصدمة الحرارية مما يوسع أفق تطوير المنتج الحراري النهائي.


Article
Annealing Effect on the phase Transformation in
دراسة تأثير التلدين في التحولات الطورية لأوكسيد التيتانيوم

Authors: Anwar A. Baker أنوار علي باقر --- Asmaa J. Khadum أسماء جواد كاظم --- Majida A. Ameen ماجدة علي أمين
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2011 Volume: 8 Issue: 2عدد خاص بمؤتمر الفيزياء Pages: 503-508
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This work describes the effect of temperature on the phase transformation of titanium dioxide (TiO2) prepared using metal organic precursors as starting materials. X-ray diffraction (XRD) was used to investigate the structural properties of TiO2 gels calcined at different temperatures (300, 500, 700) C. the results showed that the samples have typical peaks of TiO2 polycrystalline brookite nanopowders after calcined at (300 C), which confirmed by (111), (121), (200), (012), (131), (220), (040), (231), (132) and (232) diffraction peaks. Also, XRD diffraction spectra showed the presence of crystallites of anatase with low proportion of rutile phase where calcined at (500 C), while rutile phase domains at (700 C). The crystallite size of TiO2 nanopowders was calculated by Scherer's formula and showed that the crystallite size decreased and then increased with increasing the annealing temperature.

يدرس هذا البحث تأثير درجة الحرارة في التحول الطوري لأوكسيد التيتانيوم المحضر باستعمال المواد العضوية الفلزية كمواد أولية. أُستعملت تقنية حيود الأشعة السينية (XRD) لدراسة الخصائص التركيبية لجل TiO2 بعد حرقها بدرجات حرارة مختلفة (300, 500, 700) C. بينت النتائج بأن للعينات التركيب المتعدد التبلور لمادة TiO2 وبطور البروكايت عند حرقها بدرجة (300 C)، تمثلت بقمم الانعكاس (111)، (121)، (200)، (012)، (131)، (220)، (040)، (231)، (132) و (232). أظهرت أطياف حيود الأشعة السينية ايضاً وجود بلورات من الاناتيس مع نسبة قليلة من طور الروتايل بعد حرقها بدرجة (500 C)، بينما يسود طور الروتايل على التركيب البلوري عند درجة حرارة (700 C). حُسب الحجم البلوري لحبيبات TiO2 الدقيقة التركيب بواسطة معادلة شرر (Scherer) وتبين ان الحجم البلوري يقل ثم يزداد بزيادة درجة حرارة التلدين.


Article
Deposition Hydroxyapatite /Titania Composite on Ti-6Al-7Nb Alloy for Human Body Implants
ترسيب مركب من هايدروكسي ابتايت /تيتانيا على سبيكة لزراعه في جسم الانسان Ti-6Al-7Nb

Author: Dunya Abdulsahib Hamdi دنيا عبد الصاحب حمدي
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2018 Volume: 21 Issue: 4 Pages: 467-472
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

The microstructural analysis and electrochemical measurements tests were used to investigate the behaviors of (TiO2) and (HAp)-coated Ti-6Al-7Nb alloy in the SBF solution .By using RF sputtering, a thin TiO2 layer coated the substrate, while a thick layer of HAp coated the outer side of surface. The generated middle layer consist of the composite of TiO2 and HAp which is by AFM characterized as uniformly distributed coating system with nano size. The images of the scan electron microscopy (SEM) shows that there is no any cracking observed in the outer layer of tested samples due to the use of thin film TiO2 as mid lead to reduce the difference in the thermal expansion between the HAp material and Ti-6Al-7Nb substrate .The HAp upper layer significantly improve the bioactivity of the Ti-6Al-7Nb alloy. In this study, the bonding strength and the corrosion resistance was improved by using thin layer of TiO2. From electrochemical impedance spectroscopy (EIS) study Bod plot, the composite layer of TiO2 and HAp was suggested by the capacitive act as barrier layer coated substrate and prevent the relays of the ion from metallic. The results shows the values of Rox (309.2 kΩ cm2)are greater than for Rct(19.2 kΩ cm2), by assumes the presence oxide film increases for coated substrate are greater than that of uncoated, which is a result of the presence of coated film that improve the corrosion resistance of the sample.

ان التحاليل التركيبيه لطبقات الطلاء وقياسات الاختبارات الكهروكيميائية بحثت في سلوك سبيكة Ti-6Al-7Nb تيتانيوم-المنيوم –نيوبيوم المغطاة بطبقه من TiO2 و HAP بعد التغطيس في محلول مشابه لمحلول الجسمSBFf .استخدمت طبقه رقيقه من التيتانيا TiO2لتغطية الاساس وطبقه خارجيه سميكه من مادة هايدروكسيد ابتايت (HAP )وايضا طبقه وسطيه كخليط من TiO2و HAP باستخدام منظومة الترذيذ الراديوي.تم تحديد التوزيع المنتظم لطبقة الطلاء والحجم النانوي لجسيمات الطلاء بواسطة مجهر القوى الذريه (AFM). ان نتائج صور المجهر الالكتروني الماسح (SEM)تبين عدم وجود تشققات في الطبقه المرسبه ولذلك يعود للاستخدام طبقه الطلاء TiO2 الرقيقة كطبقة وسطيه بين الاساس وطبقة HAP لتقليل من الاختلاف في معامل التمدد الحراري بين الاساس وHAP)) ان استخدام HAP كطبقه خارجيه يعمل على تحسين التوافق الاحيائي لمادة الاساس.في هذا العمل,قوة التاصر ومقاومة التاكل تحسنت باستخدام طبقة طلاء رقيقه من TiO2 . ومن دراسة مطياف الممانعة الكهرو كيميائية وجد بان طبقه الخليط من TiO2 و HAP يشابه عمله كعمل المتسعه الكهربائية عملت كحاجز غطت الاساس ومنعت تحرر ايونات المادة .من ملاحظة نتائج ان مقاومة طبقة الحمايه للاوكسيد اعلى من مقاومة شحنة الانتقال .مع ملاحظة ان مقاومة التاكل تزداد بوجود طبقة الاوكسايد

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

English (5)


Year
From To Submit

2018 (1)

2017 (1)

2014 (1)

2011 (1)

2009 (1)