Preparation and Characterization of Nanoporous Zeolitic Membranes for Catalytic Applications
تحضیر وفحص خصائص الغشاء الزیولایتي النانوي المسامي لتطبیقات التحفی

Author: Talib M. Naieff Al-Bayati
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 17 Part (A) Engineering Pages: 3343-3357
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The Hydroisomerization and Hydrocracking of n-Heptane was carried out in apacked bed plug-flow zeolitic catalytic membrane reactor at a constant pressureof (100 kpa).Material was encapsulated by trimetallic 1% (Pt-Ni-Co). Thestructural and textural features for encapsulated nanoporous MCM-48 werestudied by X-ray diffraction, scanning electron microscopy (SEM), EDAX,nitrogen adsorption-desorption (BET) and FTIR. The characterizations werecarried out before and after loading.The results show that the catalytic activity evaluation in a membrane reactorrevealed that trimetallic 1 % (Pt-Ni-Co)/MCM-48 catalyst possess a high activityfor conversion of n-heptane around (83%) at 400 ºC with a maximum selectivityaround (65%) at 325 ºC.


Article
Hydroisomerization and Hydrocracking of n-Heptane over Nanoporous Trimetallic (Pt-Ni-Co/SBA-15 Catalyst)
عملية ألأزمرة والتكسيرالحراري للهبتان الاعتيادي فوق العامل المساعد النانوي المسامي ثلاثي المعادن Pt-Ni-Co/SBA-15))

Authors: Talib M.Albayati --- Aidan M. Doyle
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 18 Part (A) Engineering Pages: 36-52
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The heterogeneous hydroisomerization and hydrocracking of n-heptane was carried out within the pores of the mesoporous SBA-15 silicas, within which was encapsulated trimetallic nanoparticles of Pt-Ni-Co. The structural and textural features of the nanoporoussilicas, both with and without encapsulated nanoparticles, were characterised using small angle X-ray diffraction, scanning electron microscopy (SEM), EDAX, nitrogen adsorption-desorptionporosimetry/BET surface area analysis,Fourier-transform infrared (FTIR) spectroscopyand transmission electron microscopy (TEM).Catalytic testing was conducted using a plug-flow reactor in a catalyst testing rig under tightly controlled conditions of temperature, reactant flow rate and pressure.Species were leaving the reactor andanalysed by Gas Chromatography. The results show thatPt-Ni-Co/SBA-15 had a high activity for conversion of n-heptane (around 85%). The catalyst was found to be stable to heating and did not undergo any significant deactivation during reaction at temperatures up to 400 °C.

ان عملية الازمرة والتكسير الحراري للهبتان الاعتيادي في تفاعلات غير متجانسة (متباينة) الاطوار وبوجود العامل المساعد قد حدثت ضمن مسامات المادة النانوية المسامية SBA-15 التي تم حشوتها بجسيمات او جزيئات المعادن النانوية الثلاثية 1% (البلاتين-النيكل-الكوبلت). ان تركيب المادة النانوية المسامية SBA-15 ومميزات السطح الخارجي لها تم دراستها بواسطة الاشعة السينية XRD بالاضافة الى دراسة المسح الالكتروني المجهريSEM وتحليل نسبة العناصرEDAX. وكما تم قياس المساحة السطحية وقطر المسامات بواسطة غاز النيتروجين بعملية الامدصاص وازالة الامدصاصBET . بالاضافة الى قياس المجاميع الفعالةFT-IR وكذلك تم استخدام المجهر الالكتروني الناقل (TEM). ان جميع هذه الخصائص تم دراستها قبل وبعد عملية التحميل بالمعادن.ان عملية اختبار العامل المساعد قد اجريت في المفاعل الانبوبي وفي ظروف مسيطرة عليها مثل الضغط ، درجة الحرارة، ومعدل التدفق. النتائج اظهرت ان فعالية تقييم العامل المساعد في المفاعل الانبوبي توحي بان المعادن الثلاثية المحملة 1% (Pt-Ni-Co)/SBA-15 لها فعالية عالية اثناء تحويل الهبتان الاعتيادي بحدود 85% في المفاعل الانبوبي.اوجدت النتائج استقرارية العامل المساعد للتسخين ولم يخضع لاي عملية تعطيل مؤثرة في درجة حرارة التفاعل لحد 400 درجة مئوية.