ASSESSMENT OF FATIGUE CRACK RATE UNDER CYCLIC LOADING

Author: Muhanad Hamed Mosa
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2014 Volume: 7 Issue: 3 Pages: 254-264
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Fatigue crack growth (FCG) in structures subjected to variable amplitude (VA) loading is a complex phenomenon. Analysing of FCG rate is important for the reliable life of engineering structures. It is difficult to model all the parameters influence FCG correctly due to the random nature of the VA loading as well as the number and complexity of the mechanisms involved in the FCG problems. . It has been found from the literature review that no universal model has been developed to analyse the crack growth condition under VA loading. In addition, no general understanding has also been agreed among researchers for any available models. Therefore, the main objective of this work is to investigate the FCG under VA loading based on FCG models also to propose a suitable model for VA loading. The work describes some of the FCG models for predicting the fatigue lives and FCG rates. For the simulation part of this study, towards prediction of crack propagation under cyclic, variable and random loading were used. The results had been carried out based on the Austen, modified Forman and NASGRO models. There are many factors affecting the FCG, which shown with great influence such as; initial crack length, load sequence, aspect ratio and stress ratio.


Article
FINITE ELEMENT MESH SIZE IN FATIGUE LIFE EFFECT

Author: Muhanad Hamed Mosa
Journal: University of Thi-Qar Journal for Engineering Sciences مجلة جامعة ذي قار للعلوم الهندسية ISSN: 26645564/26645572 Year: 2016 Volume: 7 Issue: 1 Pages: 18-27
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

Pipe elbows are consequential parts in a piping system. When a thin-wall elbow is exposed to variable amplitude loading as internal cyclic pressure, piping elbows are vulnerable to crack at the crown. This paper presents a technique to predict the fatigue life of elbows with the application of variable amplitude loadings (VAL). For this goal, the finite element analysis technique was being used for the modeling and simulation. The fatigue life prognostication was carried out using the finite element based fatigue analysis codes. Numerical life prognostication results of three types of elbows (135o ,45o and curved ) under VAL are presented and discussed. Varying elbows shows different fatigue life behavior, the curved one gives better life. The two types of elements (Tet4 and Tet10) were investigated with optimum mesh size to get the maximum principle stress. The simulation results showed that more studies on the piping elbows necessity to be performed in order to obtain more delicate fatigue life.

تعتبر الانابيب الكوعية من العناصر الهامة في الانظمة الخاصة بشبكات الانابيب , فعندما يتعرض الكوع الرقيق الجدران لاحمال متغيرة السعة كالاختلافات الدورية في الضغط الداخلي لتلك الانابيب يكون عرضة الى نشوء صدع في الانبوب . يقدم هذا البحث تقنية للتنبؤ بعمر الانبوب الكوعي حيث شمل البحث مدى واسع من الاحمال المتغيرة حيث تم استخدام تقنية تحليل العناصر المحدودة للنمذجة والمحاكاة. وقد تم تنفيذ هذه الطريقة باستخدام ثلاث انواع من الزوايا لتلك الانابيب ( 45 درجة ، 135 درجة والانابيب المنحنية) و تم اجراء الدراسة والمناقشة للنتائج لهذه الانواع الثلاثة, ولقد تبين بان اختلاف الزوايا والشكل في الانابيب الكوعية يؤدي الى الاختلاف في اعمار هذه الانابيب اعتمادا على انواعها ولقد تبين من خلال هذه الدراسة بان افضلها عمرا هي الانابيب المنحنية .عند اجراء النمذجة تم فحص هذين النوعين من عناصر (Tet4 وTet10) مع الحجم الامثل للشبكة الخاصة بالعناصر المحددة وذلك للحصول على أقصى قدر من الاجهاد الاساسي او الاجهاد الاقصى ولقد وأظهرت نتائج المحاكاة ضرورة اجراء المزيد من الدراسات على الأنابيب الكوعية وذلك من أجل الحصول على نتائج اكثر دقة للتنبؤ بحياة تلك الانابيب.


Article
تأثير الاحمال الثابتة والمتغيرة السعة على عمر الكلال لسبيكة من الفولاذ المنخفض الكاربون

Author: شيماء عبد الخضر حمزة
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 1 Pages: 221-227
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research studies the growth rate of the cracks and accumulation damage of the fatigue for low carbon steel alloy with fixed and variable stresses amplitude. All tests were carried out under a stress ratio of (R=0.1) and at room temperature condition. Two test groups consisting of 12 flat samples were designed.The first group was tested under constant amplitude loads which aimed to study the rate of growth and the increasing of fatigue cracks by increasing the stresses exerted. The second group was tested under variable amplitude loads in the form of (decreasing) and (increasing- decreasing) loads. The aim was to study the effect of periodic strain ranges on the growth rate of cracks and fatigue life.The results of the constant amplitude loads proved that the increasing of the applied stress about 26% leads to reducing the fatigue strength and thus decreasing the fatigue life about 93%. In the case of the second group, which was carried under variable amplitude loads, the results were as follows: In case of variable amplitude loads in the form of (decreasing), Nf is up to 186000 cycles while in case (increasing- decreasing) loads, the number of courses required for the failure was Nf 151000 cycles.

تضمن البحث دراسة معدل نمو الشقوق وتراكم ضرر الكلال لسبيكة من الفولاذ المنخفض الكاربون تحت اجهادات حني دورية ثابتة ومتغيرة السعة وبنسبة اجهاد ثابتة مقدارها (R=0.1), حيث تم تصميم مجموعتي اختبار تضم 12 عينة مسطحة الشكل.تهدف اختبارات القسم الاول الثابتة السعة الى دراسة معدل نمو وزيادة شقوق الكلال بزيادة الاجهادات المسلطة. تضمن القسم الثاني اختبارات كلال متغيرة السعة مستقرة من نوع تحميل (متناقص) و(متزايد - متناقص), كان الهدف منها دراسة تاثير تسلسل مديات الاجهاد الدوري على معدل نمو الشقوق وعمر الكلال.ان النتائج الخاصة بالاحمال الثابتة السعة اثبتت ان زيادة الاجهاد المسلط حوالي 26% تؤدي الى تقليل مقاومة الكلال وبالتالي نقصان عمر الكلال بحوالي 93%, اما في حالة المجموعة الثانية والتي تمت تحت احمال متغيرة السعة مستقرة فكانت النتائج كالآتي: في حالة كون الحمل من نوع تزايد- تناقص وجد ان عدد دورات الفشل Nf تصل الى 186000 دورة بينما في حالة كون الحمل من نوع تناقصي فكانت عدد الدورات اللازمة للفشل Nf 151000 دورة.


Article
EXPERIMENTAL STUDY FOR THE SIZE EFFECT ON THE FLEXURAL BEHAVIOUR OF SPLWA REINFORCED CONCRETE SLABS STRENGTHENED WITH CFRP STRIPS
دراسة عملية لتأثير الحجم على تصرف الانحناء للبلاطات الخرسانية المسلحة الخفيفة والمقواة بشرائح البوليمر المسلحة بألياف الكربون

Author: رياض عبد الرضا الغرة
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2014 Volume: 3 Issue: 1 Pages: 60-74
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

An experimental Study was conducted to investigate the size effect on the flexural behaviour of sand-porcelinite lightweight aggregate reinforced concrete one way slabs (SPLWAC OWS). In order to get a clear results, eight slabs were casted, and six of them were strengthened with carbon fibre reinforced polymer (CFRP) strips. To investigate the size effect, four slabs were of 300 mm width, 1500 mm length and 80 mm depth and the others were of 300mm width, 2000 mm length and 108 mm depth. The present study showed that the SPLWAC OWS showed a reverse size effect. The failure mode was by yield of steel for the control un-strengthened slabs, while it was by yield of steel followed by rupture of CFRP strips for the strengthened slabs. Also, the results of this study were compared with those obtained by the ACI equations. This comparison showed that the ultimate moment strength and deflection obtained by the ACI equations were always less than those obtained experimentally.

يقدم هذا البحث دراسة عملية لتأثير الحجم على سلوك الانحناء للبلاطات الخرسانية المسلحة الخفيفة. لغرض انجاز البحث، تم تحضير ثمان بلاطات، ستة منها مقواة بشرائح البوليمر المسلحة بألياف الكربون. لدراسة تأثير الحجم تم تحضير اربع بلاطات بأبعاد 300 ملم عرض، 1500ملم طول و 80 ملم سمك وأربع بلاطات بأبعاد 300 ملم عرض، 200 ملم طول و 108 ملم سمك . أظهرت هذه الدراسة تأثير عكسي للحجم على تصرف الانحناء للبلاطات. كانت طبيعة الفشل بواسطة خضوع حديد التسليح في البلاطات غير المقواة، بينما كانت طبيعة الفشل بواسطة خضوع حديد التسليح يتبعه تمزق شرائح البوليمر في البلاطات المقواة. تم مقارنة نتائج هذه الدراسة مع معادلات الكود الأمريكي وأظهرت المقارنة أن تحمل العزم الأقصى والهطول المحسوب باستخدام معادلات الكود الأمريكي كانت دائما اقل من نتائج الدراسة العملية.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (3)

Arabic (1)


Year
From To Submit

2018 (1)

2016 (1)

2014 (2)