Article
Investigation of the Tribological Behavior of Eutectic Al-Si Casting Alloy

Author: Riyadh Azzawi Badr
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2017 Volume: 24 Issue: 3 Pages: 42-46
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

The effect of roughness of Al-Si alloy on the wear is investigated. Roughness average (Ra) was verified via different polishing, also was using a pin–on-disc of different loads (5, 10, 15) N, different speeds (100, 200, 300) rpm and relative humidity 74%. Different values of Ra are obtained with (3, 5 and 7) µm. Worn surface were characterized using SEM / EDX. The results show that the wear rate of Al-Si eutectic alloys increases with the roughness increase. It was noticed that the specific and wear decreases as roughness decreases. Severe wear was observed at all loads.


Article
Study the effect of diode laser on the properties of dental composite
دراسة تأثير الليزر الدايود على خصائص مادة الحشوة الضوئية للأسنان

Loading...
Loading...
Abstract

In this study anterior filling was used type of G-aenial and used in the restoration of teeth, then conducted a study and divided into four groups of the first sample, which is the group A, which was irradiated by laser and then hardened by Light Curing then irradiated with laser and the third sample C, which was irradiated with Light Curing, and the laser on the sample at the same time and the fourth sample D The original samples are not exposed to irradiation (control) Based on the filling specifications The sample was prepared cylindrical and dimensions (10 × 6mm) to be used in a number of Synthetic measurements such as x-ray diffraction analysis, electron microscopy scanner and some important mechanical properties such as hardness and wear. The results showed X-ray diffraction that the components of A, B, C and D aggregates gave emitted precipitation and a thin crystalline state clear all forms of x-ray diffraction. It was found that the XRD test of the B group showed a significant increase in the intensity of the material in the G-aenial filler and is indicated by the laser effect clearly after light therapy and laser irradiation.The results of the SEM examination of group B in the case of Light Curing and laser hardening showed clear homogeneity and better atomic distribution compared to other studied groups.

في هذه الدراسة تم استخدام حشوة أمامية من نوع G-aenial والمستخدمة في ترميم الأسنان ، بعدها أجريت عليها دراسة وقسمت إلى أربع مجاميع العينة الأولى والتي هي مجموعة A التي تم تشعيعها بليزر ثم تصليبها بالعلاج الضوئي Light Curing والعينة الثانية B والتي تم تصليبها بالعلاج الضوئي Light Curing ثم تشعيعها بالليزر والعينة الثالثة C التي تم تشعيعها بالعلاج الضوئي Light Curing والليزر على العينة في نفس الوقت والعينة الرابعة D العينات الأصلية الغير معرضة للتشعيع (الكونترول) واستنادا على مواصفات الحشوة تم تحضير العينة بشكل اسطوانية وبأبعاد 10×6mm)) وتم استخدامها في عدد من القياسات التركيبية مثل تحليل حيود الأشعة السينية والمجهر الألكتروني الماسح وبعض الخصائص الميكانيكية المهمة مثل الصلادة والبلى. وأظهرت نتائج حيود الأشعة السينية أنﱠ المكونات للمجاميع A,B,C,D أعطت قمماً مستطاره منبعثة وبحالة بلورية نحيفة Crystalline)) واضحة لجميع أشكال حيود الأشعة السينية . بينت النتائج أن فحص XRD لمجموعة B حدث فيه ارتفاع كبير في الشدة للمواد في حشوة G-aenial وذلك نتيجة لتأثير الليزر بشكل واضح بعد إجراء المعالجة بالضوء ثم التشعيع بالليزر. وأظهرت نتائج الفحص المجهري SEM للمجموعة B في حالة المعالجة بالضوء ثم التصليب بالليزر تجانساً واضحاً وأفضل توزيع ذري مقارنة مع المجاميع الأخرى المدروسة.