Article
Mechanical Properties of MIG Joints for Dissimilar Aluminum Alloys (2024-T351 and 6061-T651)
الخواص الميكانيكية لوصلات لحام القوس الكهربائي (MIG) من سبائك الالمنيوم غير المتشابهة (2024 T351, 6061-T651)

Author: Nawres Jabar Nasser نورس جبار ناصر
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2016 Volume: 12 Issue: 3 Pages: 121-128
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The research aims to investigate the effects of GMAW or MIG welding process on the mechanical properties of dissimilar aluminum alloys 2024-T351 and AA 6061- T651. A series of experimental techniques have been conducted to evaluate mechanical properties of the alloys, by carrying out hardness, tensile and bending tests for welded and un-welded specimens.Metal inert gas (MIG) has been carried out on sheet metal using ER- 4043(AlSi5) as a filler metal and argon as shielded gas. The welded joints were tested by X-ray radiography and Faulty pieces were excluded. Welding joints without defects are subjected to heat treatment including heating the joints in furnace to 170 °C for half an hour then air cooling to relief welding stress.Tensile test was implemented for all specimens which prepared in the dimensions according to ASTM 17500 by using Testing machine smart series with preload value 100 kN. Vickers hardness test and microstructure examination were made, the last test was bending test which implemented on the welded and un welded specimens which machined into standard test specimen dimensions. Results of mechanical properties Using MIG welding process appear a general decay compared with un welded and in the dissimilar joint comparing with parent metal that is due to the microstructure change during the welding process. The location of the failure for welded specimens after all mechanical test was found predominantly along the heat affected zone ( HAZ ).but Unwedded specimens were failed near the center line of the specimen.

يهدف البحث الى بيان تاثير طريقة لحام القوس الكهربائي المحمي بالغاز على الخواص الميكانيكية لسبائك غير متماثلة من سبائك الالمنيوم عالية المتانة هما -T32024 , 6061-T6 حيث تضمن البحث اجراء سلسلة من التجارب التقنية لتقييم الخواص الميكانيكية للسبائك الملحومة وغير الملحومة وهي خصائص الشد و الصلادة, والحني والبنية المجهرية .انجز اللحام على صفيحتين من السبائك اعلاه للحصول على وصلات تناكبية بالابعاد 200)*100*8) ملم بعد عمل زاوية تحضيرية من جهة واحدة مقدارها 70 درجة حرف(V) ووصلة اخرى بنفس الابعاد بدون زاوية باستخدام سلك لحام 4043 ER والاركون كغار حماية بعد عملية اللحام والتاكد من خلو الوصلة من العيوب من خلال فحصها بواسطة جهاز X-ray radiographyاجريت معاملة حرارية تضمنت تسخين الوصلة في فرن كهربائي عند درجة حرارة 170 درجة مئوية لمدة نصف ساعة ثم التبريد بالهواء بهدف ازالة اجهادات اللحام .تم تحضير عينات اختبار الشد من وصلات اللحام والمعدن الاساس وفق المواصفة القياسية ASTM17500 وكذلك عينات اختبارالحني وفق المواصفةASTM (E 190-92) ثم اجراء عمليات تحضير من تنعيم وصقل لغرض فحص البنية المجهرية لمناطق اللحام والمعدن الاساس واجري اختبار صلادة عيانية, وصلادة دقيقة لبيان تأثير اللحام على الخواص الميكانيكية .اظهرت النتائج انخفاض في الخواص الميكانيكية للعينات الملحومة مقارنة بالمعدن الاساس وللسبائك غير متماثلة مع السبيكه الاساس وان موقع الفشل في منطقة الوسط للعينات اما العينات الملحومة فقد ظهر الفشل في المنطقة المتاثرة بالحرارة.


Article
THE EFFECT OF SHOT PEENING ON BENDINGSTRENGTH FOR MIG WELD JOINT ALUMINUM ALLOYS 2024 T351
تأثير القصف بالكرات على مقاومة الانحناء لسبائك الالمنيوم 2024 T 531 الملحومه بطريقة MIG

Author: Muammar Ibrahim Ismail معمر ابراهيم اسماعيل
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2017 Volume: 30 Issue: 1 Pages: E60-E78
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

Theinfluence ofshot peening onbending strength using MIG welding joint aluminum alloys 2024-T351 was studied. The paper implements many series of experimental techniques to figure the bendingstrength of all specimens , by performance hardness, shot peen, remaining stress and bending examinations for un-joint and joinedsamples. (MIG) process has implemented onsheets of "8mm thickness" to getbutt joiningconnections with measurement of (200 *100* 8) mm with joining readying angle in formsingle and double V of 75⁰and flatjoinby "ER- 4043(Al-Si5)"as a "groutmetal"and "argon" as protected gas. The juncturesareexamined by"X-ray radiography"and exceptedtheimperfect joint, then Welding joint exposed to heat treatment to removed joiningresidual stress.Hardness was measured using Vickers test and the specimens microstructure were examined, finally bending testimplemented on the samples which fabricated into typicalexaminationsample dimensionagreeing to the ASTM (E 190-92) of welded and un welded joints, and then ejaculation by steel ball in diameter 1.25 mm for 10 min to show the influence of shot peening on weld bendingThe Results of bendingqualities for MIGweld connected showdecay when comparing it with theunwedded joints and chiefly along the HAZ .but unweddedsamples were fiascoes nigh the middle line of the sample shot peening contributed in improvement of bending process for all specimens. Ansysprogram was used to conduct stress analysis operations.

درس هذا البحث تاثير طريقة القذف بكرات فولاذية على مقاومة الحني لسبيكة من سبائك الالمنيوم عالية المتانة هي T3512024 تم لحامها بطريقة القوس الكهربائي المحمي بغاز خامل وقد اجريت سلسلة من التجارب التقنية لتقييم مقاومة الحني للسبيكة تضمنتكل من اختبارات الصلادة, القذف بالكرات , الاجهادات الضغطية و البنية المجهرية للعينات الملحومة وغير الملحومة .انجز اللحام باستخدام لحام القوس الكهربائي المحمي بغاز على قطعتين من السبيكةالتي تم ذكرها بهدف انتاج وصلات تناكبية بالابعاد8)*( 200*100ملم اذ تم كسر حافات القطع من جهة ومن جهتين بزاوية مقدارها75درجة على شكل حرف Vووصلات بدون زوايا تحضيرية بواسطة سلك لحام رمزه4043 ERوالاركون كغار حمايةبعد عملية اللحام تم التاكد من عدم احتواء الوصلة على العيوب حيث تم فحصها بواسطة جهاز X-ray radiographyثم اجريت معاملة حرارية لغرض التخلص من اجهادات اللحام المتبقيه.صنعت عينات اختبار الحني من وصلات اللحام والمعدن بدون اساس اعتمادا على الابعاد القياسية ASTM (E 190-92) وكذلك اجراء عمليات فحص البنيةالمجهريه ,تم تعريض العينات الى القذف بكرات فولاذية قطرها 1.25mm وصلادة RC 55Hوبزمن 10 دقائق لبيان تاثير عملية القذف بكرات فولاذية على مقاومة الحني. للعينات الملحومة وغير الملحومة ومن النتائج التي تم الحصول علبها وجد ان القذف بكرات فولاذية ساهم في تحسين مقاومة الحني للعينات الملحومة من خلال معالجة عيوب اللحام . وتم استخدام برنامج Ansys لاجراء عمليات تحليل الاجهادات